结晶器铬锆铜板表面等离子喷涂镍铬-碳化铬涂层的分析-analysis of plasma spraying ni - cr - cr carbide coating on the surface of crystallizer cr - zr copper plate.docxVIP

下载本文档

6
0
约6.81万字
约 79页
2018-05-29 发布于上海
举报
版权申诉

结晶器铬锆铜板表面等离子喷涂镍铬-碳化铬涂层的分析-analysis of plasma spraying ni - cr - cr carbide coating on the surface of crystallizer cr - zr copper plate.docx

1、本文档共79页，可阅读全部内容。
2、原创力文档（book118）网站文档一经付费（服务费），不意味着购买了该文档的版权，仅供个人/单位学习、研究之用，不得用于商业用途，未经授权，严禁复制、发行、汇编、翻译或者网络传播等，侵权必究。
3、本站所有内容均由合作方或网友上传，本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺！文档内容仅供研究参考，付费前请自行鉴别。如您付费，意味着您自己接受本站规则且自行承担风险，本站不退款、不进行额外附加服务；查看《如何避免下载的几个坑》。如果您已付费下载过本站文档，您可以点击这里二次下载。
4、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等，请点击“版权申诉”（推荐），也可以打举报电话：400-050-0827(电话支持时间：9:00-18:30)。

结晶器铬锆铜板表面等离子喷涂镍铬-碳化铬涂层的分析-analysis of plasma spraying ni - cr - cr carbide coating on the surface of crystallizer cr - zr copper plate

coefficientofthermalexpansionbetweencoatingandsubstrate.Formsstressconcentrationandthethermalfatiguecracksintheinterfacefromtheangleofthespecimen,crackpropagationcausethecoatinginterfacialdebonding.Inaddition,theoxidationoftheinterfacepromotesthermalshockfailure.Themainfailuremoldsforthecoatingarethecracksofthecoatinginitiate,expandandthenoverallpeelfromtheinterfacealongthecoatingandsubstrate,andthefailureofsmallpiecesoff,moreover,failuremoldsareassociatedwithtemperature.Thecoatingsarewellbondedandhavelowporosity.ThereisexothermicreactionbetweenNiandAlduringtheprocessofplasmasprayingtheNiAlcoating，andvariouskindsofintermetallicssuchasAl4Ni3,Al3Ni2,AlNi3andsoonareformedatthesametime.TheremainingAlcanreactwithCusubstratetoformCu3Al2、CuAl2andCuAl，thusthereisamicro-metallurgicalbondinginsomemicro-zonebetweenthecoatingandsubstrate,butthebondingwasmainlymechanicalbonded.Bothintheparallelandperpendiculardirectionscomparedwithsubstrate,themicro-hardnessofCr3C2-NiCrcoatingandNiAlcoatinghasgreatlydispersion.Butintheparalleldirectiontosubstrate,theysignificantlyconformtonormalandweibulldistribution.Throughthevacuumdiffusionheattreatment,solutiontreatmentandthenagingtreatment，notonlyhardnessandelectricalconductivitycanbecompletelyrecoveredtomeettheCuCrZralloys’performancewhicharecalledformould,butalsocansignificantlyincreasebondingstrengthofcoating.Comparedwiththenon-heattreatmentcoating,thebondingstrengthofexperimentalcoatingincreased4.43times.Keywords：plasmaspraying；CuCrZralloy；orthogonaltest；bondingstrength；Cr3C2-NiCrcoating；vacuumdiffusiontreatment；thermalshockstest论文独创性声明本人声明所呈交的学位论文是我本人在导师指导下进行的研究工作及取得的研究成果。尽我所知，除了文中特别加以标注和致谢的地方外，论文中不包含其他人已经发表或撰写过的研究成果，也不包含为获得江苏科技大学或其它教育机构的学位或证书而使用过的材料。与我一同工作的同志对本研究所做的任何贡献均已在论文中作了明确的说明并表示谢意。学位论文作者签名：日期：学位论文使用授权声明江苏科技大学有权保存本人所送交的学位论文的复印件和电子文稿，可以将学位论文的全部或部分上网公布，有权向国家有关部门或机构送交并授权其保存、上网公布本学位论文的复印件或电子文稿。本人电子文稿的内容和纸质论文的内容一致。除在保密期内的保密论文外，允许论文被查阅和借阅。研究生签名：导师签名：日期：日期：第1章绪论1.1引言在炼钢生产中，连铸具有高效、节能的特点，已成为现代钢铁工业中一种常规的生产技术，如2007年中国粗钢产量4.89亿吨，连铸坯产量4.74亿吨，