AEA膨胀混凝土在建筑施工中应用 　　摘要：本文通过在某工程采用AEA膨胀混凝土施工，, 并在施工加强带时采用AEA膨胀混凝土取代后浇带，这样既能增加混凝土的密实度，还通过设置膨胀混凝土加强带,取消了原先设计的温度应力收缩后浇带,实现了连续浇筑,提高了结构的整体性，确保混凝土结构的抗裂防渗功能，还能提高混凝土强度、增强抗渗性。 　　关键词：AEA膨胀混凝土施工方法 　　Abstract: in this article, through in a project using AEA expansive concrete construction, and strengthen the construction with AEA expansive concrete instead of the pouring belt, such already can increase the concrete density, through setting expansion concrete reinforcing band, cancel the original design of the temperature stress contraction of the pouring belt, realize the continuous casting, improve the structure of the integrity, to ensure the concrete structure percolating-proof functions, but also can improve the strength of concrete, enhance penetration-proof quality. 　　Keywords: AEA expansive concrete construction method 　　 　　 　　中图分类号： TU528文献标识码：A文章编号： 　　 在广州市越秀区的某建筑工程，其建筑总面积约32000平方米，建筑总高度为57米，内有地下室一层、裙楼一层、地上18层分为两座塔楼。地下室平面形状为直角梯形，而施工图纸要求地下室至裙楼部分要设置一条后浇带。但是多年施工实践证明，后浇带作为一个后续工序，无疑增加了砼结构的施工冷缝，在实际施工过程中，由于诸多因素的影响，这些施工冷缝将带来裂缝、渗水的隐患。而采用掺入膨胀剂的砼加强带采取同时浇筑的施工方法，既可起到补偿混泥土收缩的作用，又避免了施工冷缝的出现，同时缩短了裙楼以下部分的施工工期。所以在该工程图纸会审阶段时，经多方商议确定采用加强带替代后浇带的施工方案，膨胀剂经设计确定采用AEA，内掺量为8%~12%，具体掺量通过砼试配结果确定，基本原则是在满足砼性能要求的前提下，采用最低掺量。 　　 AEA膨胀混凝土的基本性能 　　 AEA膨胀剂属于硫铝酸钙类膨胀剂，以水化硫铝酸钙即钙矾石为膨胀源或主要膨胀源。在砼中因化学反应而产生膨胀效应的水化硫铝酸钙，在钢筋作用约束下，这种膨胀转变成压应力，???少或消除砼干缩和凝缩时的体积缩小，从而改善砼质量。与此同时，生成的钙矾石等晶体具有立填、堵塞砼毛细孔阵的作用，提高砼抗渗能力。 　　 AEA膨胀剂由一定比例的高铝熟料：天然明矾石、石膏共同粉磨制成，其化学成分特点是CaO含量几乎比VEA多倍，碱含量比后者少1/2。AEA组分中高铝熟料的铝酸钙矿物Ca等首先与CaSO4、Ca(OH)2作用，水化生成水化硫铝钙（钙矾石）而膨胀。 　　 掺AEA膨胀剂的水泥物理性能见表1。 　　 　　 　　 从表2可见，掺入AEA的混凝土在水化和硬化过程中产生膨胀效应，主要发生在14天以前，14~16天仍有少量膨胀。从表3可见，掺AEA的混凝土的水化热比普通混凝土显著减少，从而减少或防止结构产生裂缝。 　　 　　 　　 主要施工技术 　　2．1膨胀混凝土加强带的设置 　　 AEA膨胀混凝土加强带设在收缩应力集中的地方，与规范须留的伸缩或后浇带位置相当。加强带的间距一般控制在30~60m。膨胀加强带的设置和做法见附图。加强带的宽度一般为2~2.5m，带的两侧分别设置快易收口网或oslash;5~oslash;8?铁丝网，既防止两侧混凝土流入加强带，同时限制两边混凝土的收缩应力，快易收口网与上下层水平钢筋及竖向加固筋绑扎或焊接牢固。 　　 　　2.2 AEA膨胀混凝土的施工方法 　　 为确保工程质量，AEA膨胀混凝土施工除遵守普通混凝土施工规范外，还必须注意以下几点： 　　 1）水泥和AEA膨胀剂等主要原材料进场有出厂合格证和进场检验报告，并需符合质量要求。 　　 2）砂、石级配