真空压浆施工技术应用.docVIP

真空压浆施工技术应用 　　 摘要：在桥梁施工中，对后张法预应力管道压浆一般采用传统的压力注浆方法。传统压浆工艺普遍存在着压过的浆体不密实,容易产生离析,干硬收缩,产生孔隙，导致预应力筋受到锈蚀的缺陷。新型的真空压浆工艺克服了普通压浆的一些缺陷，增加了浆体的强度和致密性，减少了对钢绞线的锈蚀，取得了很好的效果。本文着重从工艺、材料、设备、效果、注意事项等方面介绍真空压浆新工艺。 　　 主题词：桥梁工程；后张法预应力管道压浆；真空压浆 　　Abstract: In the bridge construction of prestressed pipe extent grouting method generally uses the traditional pressure grouting method. Traditional grouting process generally have the pressure paste imperfect, easy to produce the segregation, dry shrinkage, produce the pore, leading to the defects of the prestressed reinforcement from rust. New type of vacuum pressure grouting technology overcome the common pressure some of the pitfalls of slurry, increased the strength of paste and dense sex, reduce the corrosion of steel strand and good results have been achieved. This article emphatically from the craft, material, equipment, the effect, the points for attention in this new process vacuum pressure grouting. 　　Key Words: bridge engineering; method of prestressed pipe after-grouting; vacuum pressure grouting 　　 　　 中图分类号：U445文献标识码：A文章编号： 　　1、工程简介及真空注浆原理 　　 新建武汉天兴洲公铁两用长江大桥是国家“十五”重点项目之一。该桥位于既有武汉长江二桥下游9.8Km处天兴洲江段。长江北汊主桥为三向预应力连续梁和双向预应力简支箱梁，为提高桥梁结构的耐久性，通过做孔道压浆试验，确定后张预应力管道注浆采用真空注浆工艺。 　　 早在上世纪90年代，欧洲和北美已经普遍采用真空灌浆技术，取得了良好的效果；近年来，我国部分大型桥梁也开始使用真空压浆工艺。真空压浆就是在接近真空的状态下进行压浆，即通过抽真空手段，使预应力管道内的真空度达到80％以上，管内形成-0.08～－0.1MPa左右的负压，然后通过压浆设备以一定的压力将水泥浆压入预应力管道，通过“吸”与“压”相结合，在管道内形成致密高强的浆体，使孔道注浆取得良好的效果。 　　2真空压浆的优点 　　 和以往的普通压浆工艺相比，真空压浆由于工艺上的改进和水泥浆性能的改善，使施工质量大为提高。主要表现在以下几个方面： 　　 （1）可以消除普通压浆法引起的气泡，增强了浆体的密实度。 　　 （2）孔道在真空状态下，减小了由于孔道高低弯曲而使浆体自身形成的压头差，便于浆体充盈整个孔道。 　　 （3）采用真空压浆，其水泥浆的性能可以大大改善，水灰比大幅减小，浆体强度可以达到很高的程度。 　　 （4）真空压浆的工艺要求采用高强高密度耐高温的聚乙烯塑料波纹管，其良好的绝缘性能可以有效减少钢绞线的电化腐蚀，从而提高预应力结构的安全性和耐久性。 　　3、真空注浆工艺的设备及材料要求 　　 3.1 设备要求 　　 使用此项新工艺的前提条件是采用配套的预应力锚具组装件、成孔性能良好的塑料波纹管，使用专用设备抽、压设备、专用浆体外加剂。 　　真空压浆的关键是真空度的实现。真空度的实现通过抽真空设备以及密封系统来完成，所以必须增加一套抽真空设备和必要的密封部件。准备设备有；（1）快速有效的制浆设备；（2）真空泵；（3）压力容器；（4）进口、出口、排气口的截止阀；（5）预应力和非预应力两端的密封组件；（6）高效的压浆设备。 　　 3.2材料要求 　　 （1）能承受高负压符合要求的塑料波纹管。 　　 （2）