钢筋气压焊施工技术在黄河羊曲水电站建设中应用 　　摘要：钢筋气压焊接头强度高，质量可靠；节约能源；设备轻巧，操作简便；效率高，成本低；可全位置焊，通用性强，是一种多快好省的钢筋连接方法，钢筋气压焊技术自2010年6月在黄河羊曲水电站对外交通工程进行生产性试验后，至2012年3月在羊曲水电站建设中全面推广使用，取得了显著的技术经济效果。 　　 关键词：钢筋气压焊施工技术 经济效益 　　Abstract: the reinforced air pressure welding head strength, high quality and reliable; Save energy; Equipment and easy operation; High efficiency, low cost; Can all position of welding, versatility, is a province is the rebar connection method, reinforced air pressure welding technology since 2010 June HuangHeYang song hydropower station in foreign traffic engineering on the productive after test, to March 2012 sheep song in the construction of hydropower station in comprehensive promotion use, and achieved significant technical and economic effect. 　　Keywords: reinforced air pressure welding construction technical and economic benefits 　　中图分类号：TU74 文献标识码：A文章编号： 　　 　　 　　压焊接头工艺原理 　　 钢筋气压焊是利用氧――乙炔火焰把结合面及附近金属加热至塑化状态同时施加适当压力，由于加热和加压使结合面附近被焊金属产生了强烈的塑性变形，促使结合面接近原子间的距离，进入原子力作用范围，实现原子间互相嵌入，扩散及键合，并在热变形过程中完成晶粒重新组合的再结晶过程而获得牢固接头。 　　 由于气压焊系利用母材本身连接不需焊条或溶剂等熔敷金属，几乎不存在降低接头机械性能的杂质等有害缺陷，在气压焊过程中高温停留时间短暂，与其他焊接方法比较，气压焊对母材金属的力学性能和物理性能影响较小，组织良好、结合牢固。 　　压焊设备 　　2.1供气装置：包括氧压瓶、熔解乙炔气瓶、减压器（表）、干式回火防止器气管及接头。 　　2.2钢筋气压焊机利用日本国日本岩石公司生产的半自动气压焊机，它主要有：加压器、加热器、顶压油缸、钢筋支持夹具等组成。 　　 加压器为HG-R4电动油压式，压力为700kg/cm，输出功率400w。 　　 外形尺寸325×170×230（长×宽×高），重15kg?? 　　 加热器（环形燃烧器）3种:25型（8个喷嘴），32型（12个喷嘴），38型（12个喷嘴）。分别用于Ф25、Ф28、Ф32、Ф36钢筋焊接，火焰中心温度3000°C以上。 　　 顶压油缸为TS-RE型，断面积10cm2，行程55mm，重1.5kg。 　　 钢筋支持加具分不同规格，可夹Ф51mm以下变形钢筋或Ф60mm以下圆钢，重约10kg，一般采用国内加工。 　　3.焊接工艺流程及参数 　　3.1流程 　　 　　 　　 　　3.2参数 　　 ①氧气作业压力0.6Mpa，乙炔作业压力0.1-0.15Mpa（2-3瓶并联）。 　　 ②接合面局部间隙小于5mm。 　　 ③平均加热时间 　　 钢筋直径（mm）Ф25、Ф28、Ф32、Ф36 　　 时间（秒） 50、65、90、110 　　 ④加热幅度：接合面两端各一倍D范围（D为钢筋直径）。 　　4.质量保证和质量验收 　　4.1质量保证 　　 ①气压焊工必须经过培训与考试，按国家标准《钢筋气压焊》GB12219-89附录中在关规定执行，持证上岗。 　　 ②雨雪天风速超过5.4M/S时，在没有防护措施的情况下，不进行气压焊作业;气温低于-20℃时,不得进行焊接。 　　 ③必须保证钢筋端面清洁露出金属光泽。 　　 ④填写气压力焊报告，包括施工情况记录与抽样试验报告，如实记录当班焊接日期，气候，压接工程部位，钢筋规格，接头数量，作业中出现的异常情况及处理办法，外观检查情况和焊工姓名等。 　　4.2质量验收 　　 ①