双向拉伸预应变车身高强度钢板材高速率成形性能分析-analysis of high-speed forming performance of bi-directional pre-strained body high-strength steel sheet.docxVIP

下载本文档

15
0
约4.01万字
约 65页
2018-07-31 发布于上海
举报

双向拉伸预应变车身高强度钢板材高速率成形性能分析-analysis of high-speed forming performance of bi-directional pre-strained body high-strength steel sheet.docx

双向拉伸预应变车身高强度钢板材高速率成形性能分析-analysis of high-speed forming performance of bi-directional pre-strained body high-strength steel sheet

AbstractEnvironmentalprotection,safetyandenergyefficiencyarethethreemajorproblemsintheautomotiveindustry.Withafurtherincreaseintheautomotiveindustrydevelopmentandthepressureontheenvironment,environmentandenergyissuesarebecomingtheimportantproblemsinautomotiveindustryespeciallyinrecentyears.Withtheapplicationofhighstrengthsteel,automotivelightweightingcaneffectivelyreducevehicleweightandimprovesafety.However,highyieldstrengthandtensilestrengthofthehigh-strengthsteelmakeitmoreeasilytoruptureandreboundthanregularsteelandthestabilityofthepartsizeandshapedeteriorates.Therefore,theresearchanddevelopmentprocessingofadvancedhighstrengthsteelsheetsforautomotivebodyarecurrentlykeyissuestoenhancingitsformabilityandexpandeditsscopeofapplication.Electromagneticformingisonekindofhighvelocityforming,whichreleaseenergyinashorttimeandmakethemetalformingwithimpulseimpactpressure.Comparedtotheotherhighvelocityformingelectromagneticformingcanimprovetheformabilityofthemetal,itisofgreatsignificanceintheresearchofprocessforadvancedhighstrengthsteel.What’smore,thecombinationofhighstrainrateformingandgeneralprocessingtechniquedemonstrateitstechnicaladvantagesbetter,anditismorevaluableinapplications.Inthispaper,theresearchobjectsaredual-phasesteelDP590andB280VK.thestampingformingparametersofthematerialswereobtainedbythequasi-statictensileexperimentsandcuppingtest.TheinfluenceofbiaxialtensileprestrainfortwokindsofAHSSunderelectro-magnetichighstrainratebulging,stretchingtotheformabilityandthemicrostructu-rewereinvestigatedbythecombinationofbiaxialtensilepre-strainandelectromagneticforming.Thepre-strainhaveasignificantimpactontheformabilityofthesheet.ntheexperimentofelectromagnetichigh-speedstretch,thepre-strainwiththesamedirectionwithhigh-speedtensileincreasesforminglimitofThefinaldeformation,buttheVerticalpre-strainreducesit.theferriteisshapedbypre-strainandthedistributionofmartensitealsochanged,thentheformabilityofthematerialchanged.Theapplicationsofthecombinativeprocessofbiaxialtensilepre-s

您可能关注的文档

文档评论（0）

1亿VIP精品文档

更多 >

双向拉伸预应变车身高强度钢板材高速率成形性能分析-analysis of high-speed forming performance of bi-directional pre-strained body high-strength steel sheet.docxVIP