水溶液电池负极材料liti2po43c的合成及其性能研究-synthesis and properties of liti 2 po 43 c as cathode material for aqueous battery.docxVIP

methodlikeLiTi2(PO4)3/C，andusethismaterialasanegativeelectrodeofaqueoussolutionofsodiumionbattery.NaCoO2asapositiveelectrode，2mol/LNa2SO4aselectrolyteassembleNaCoO2/2mol/L，Na2SO4/NaTi2(PO4)3／Caqueoussolutionofsodiumionbattery.Testingitselectrochemicalpropertiesatdifferentrates，thematerialhasanexcellentcapacityretentionratioasthecapacityretainsmorethan80%after100cycles.TheresultdemonstratedthattheNaTi2(PO4)3／Chasaperfectelectrochemicalperformance.WhetherLiTi2(PO4)3/CorNaTi2(PO4)3/C，theyallhavetheperfectelectrochemicalperformanceinaqueouselectrolyte，butrelativelypoorcycleperformancecomparedwithorganicsystem.Keywords:aqueouslithiumbattery，LiTi2(PO4)3／C，NaTi2(PO4)3/C，High-temperaturesolid-statemethod，negativeelectrode目录中文摘要..........................................................................................................................................I英文摘要.......................................................................................................................................III1绪论..............................................................................................................................................11.1锂离子电池发展简史...............................................................................................................11.1.1锂离子电池的基本原理....................................................................................................21.1.2锂离子电池的主要特点及其应用....................................................................................31.1.3锂电池的结构....................................................................................................................41.2水溶液锂离子电池...................................................................................................................51.2.1水溶液锂离子电池的工作原理........................................................................................61.2.2水溶液锂离子电池的理论基础........................................................................................71.2.3水溶液钠离子电池的理论基础.............