时效对2219铝合金vptig焊接结构性能影响分析-effect of aging on structural properties of 2219 aluminum alloy vp tig welding.docxVIP

ThetwoprincipalinfluencingfactoroffatiguelifeofT-jointarestressconcentrationinweldtoeandresidualstressofweldingjoint.Thegreaterknuckleradiusofjointwas,thelowerconcentrationfactorwasandthelongerthefatiguelifewas.FatiguestrengthofweldedT-jointwas71MPa.AndthefatiguestrengthoftheagingweldedT-jointwas89MPa,whichincreasedby26%.Inconclusion,thefatiguelifeimprovedafterartificialagingbecauseofthereleaseofresidualstressandrecoveryofstrength.Keywords：2219aluminumalloy;T-weldedstructrue;Artificialagingtreatment;Procedurequalification;Intergranularcorrosion;Fatiguelife目录目录............................................................................................................................I第一章绪论..................................................................................................................11.1选题背景及研究意义............................................................................11.2整体壁板焊接研究现状........................................................................31.2.1国内外研究现状..........................................................................31.2.2T型接头焊接方法41.32219铝合金焊接结构及其焊后时效研究现状....................................61.3.12219铝合金焊接结构的力学性能..............................................61.3.22219铝合金抗腐蚀性能研究......................................................71.3.32219铝合金结构疲劳性能研究..................................................81.4课题研究内容及方法..........................................................................10第二章基本原理及实验材料....................................................................................112.1铝合金时效原理..................................................................................112.1.1铝合金时效基本原理................................................................112.2试验条件..............................................................................................142.2.1试验材料....................................................................................142.2.2焊丝成分........................................................................