重庆大学硕士学位 重庆大学硕士学位论文 英文摘要 PAGE PAGE VI content of Portland cement increase, the flexural strength and corrosion resistance firstly increased and then decreased at the age of 28d. The optimal content of Portland cement is 6%. In this dosage, the flexural strength and corrosion resistance are the best, and the water absorption is larger. But its age of hydration is too long, so it does not apply to mold gypsum. In summary, the best cement for mold gypsum is sulfur aluminate cement and the optimum dosage is 6%. Key words: mold gypsum, admixture, strength, cement, corrosion resistance 重庆大学硕士学位论 重庆大学硕士学位论文 目 录 目 录 中文摘要I 英文摘要 II HYPERLINK \l _bookmark0 1 绪 论 1 HYPERLINK \l _bookmark1 1.1 我国陶瓷工业的现状和发展前景································································1 HYPERLINK \l _bookmark2 1.1.1 我国陶瓷产量 1 HYPERLINK \l _bookmark3 1.1.2 陶瓷加工工艺 1 HYPERLINK \l _bookmark4 1.1.3 陶瓷模具的分类 3 HYPERLINK \l _bookmark5 1.2 模具石膏的发展概况 ···············································································4 HYPERLINK \l _bookmark6 1.3 发展模具石膏的意义 ···············································································4 HYPERLINK \l _bookmark7 1.4 国内外陶瓷模具石膏的研究现状·································································5 HYPERLINK \l _bookmark8 1.5 影响模具石膏质量的主要因素····································································7 HYPERLINK \l _bookmark9 1.5.1 石膏模具存在的问题 7 HYPERLINK \l _bookmark10 1.5.2 影响模具石膏质量的主要因素 8 HYPERLINK \l _bookmark11 1.6 本课题的研究内容与研究目的 ································································ 10 HYPERLINK \l _bookmark12 1.6.1 主要研究内容 10 HYPERLINK \l _bookmark13 1.6.2 本课题的研究目的 11 HYPERLINK \l _bookmark14 1.7 本课题的研究意义··············································································· 11 HYPERLINK \l _bookmark15 2 原材料及试验方法 12 HYPERLINK \l _bookmark16 2.1 原材料 ····························································································· 12 HYPERLINK \l _bookmark17 2.1