CFG桩软基处理分析 　　摘要:CFG 桩目前具有处理地基技术具有适应性、承载力高等特点。但其理论研究与实际施工过程中仍存在差异，尤其是混合量配合比设计、参数确定、复合地基承载力的计算方法等还有许多不完善的地方。结合某在建工程，通过理论设计、现场试验检验两方面进行了对比分析，提出了设计时相关参数的合理采用。 　　关键词:CFG 桩; 配合比; 设计参数; 地基承载力;沉降计算 　　Abstract: CFG pile has the technology of foundation treatment with adaptability, high bearing capacity characteristic. But the theory research and actual construction process there are still some differences, especially the mixed volume mixing ratio design, parameter determination, composite foundation bearing capacity calculation methods have many imperfect places. Combined with a project under construction, through theoretical design, field test inspection two aspects has carried on the contrast analysis, puts forward the design parameters related to the rational use of. 　　Key words: CFG pile; mixture ratio; design parameters; bearing capacity of foundation; settlement calculation 　　中图分类号：TU473.1文献标识码：A 文章编号： 　　 　　引言 　　水泥粉煤灰碎石桩(Cement Flyash Gravel Pile,以下简称CFG桩)是在碎石桩基础上加进一些石屑、粉煤灰和少量水泥，加水拌和制成的一种具有一定粘结强度的桩，和桩间土、褥垫层一起形成复合地基，处理技术具有适应性广、承载力高、经济合理等特点。但其理论研究仍落后于实践，尤其是混合量配合比设计、参数确定、复合地基承载力的计算方法等还有许多不完善的地方。由于影响实际施工的因素众多，各因素又互相作用，完全靠理论分析方法很难得出准确的计算公式，现在设计人员广泛使用的《规范》公式和其他理论公式是借助于试验基础上的半经验半理论公式，经验系数的取值对计算结果产生很大影响。在实际工程中，设计往往偏于保守，施工单位施工水平良莠不齐。因此，合理确定CFG桩的各种参数和明确具体参数要求已成为CFG 桩复合地基设计的重要问题。 　　一、CFG 桩的配合比设计 　　1.1 CFG桩身材料 　　CFG桩水泥一般用42.5级普通硅酸盐水泥。如用高标号水泥，则会使水泥用量偏少，影响和易性及密实度;如用低标号水泥，则会使水泥用量过多，不经济，而且也会影响混合料其它技术性能。粉煤灰多用袋装的Ⅱ级、Ⅲ级粉煤灰，粉煤灰既是细骨料，又有低标号水泥的作用，以增加桩体的后期强度。碎石粒径20～50 mm，为使级配良好，掺入石屑填充碎石的空隙。外加剂可根据施工需要采用早强剂或泵送剂。 　　1.2混合料配合比设计 　　混合料配合比基于要求的坍落度和强度进行设计，强度以28d强度为准。 　　1) 确定用水量W 　　用水量由坍落度具体值试配确定，一般从经验用水量开始;令单方用水量为w。 　　(2) 确定水泥用量C 　　根据采用的水泥标号Rcb，混合料28d强度#402;cu， 　　 #402;cu=0.366Rbc(C/W－0.071)……………… (1) 　　 式中:#402;cu—混合料28d强度(MPa)，由边长150mm的立方体试块测得;Rcb—水泥标号(MPa)；C—单方水泥用量(kg)；W—单方用水量(kg)。 　　(3) 确定粉煤灰用量F 　　单方粉煤灰用量按式计算: 　　W/C=0.187+0.791F/C ………………… (2) 　　(4) 石屑用量G1和碎石用量G2 　　计算单方石屑用量G1和单方碎石用量G2需要用到石屑率λ： 　　λ= ………………………………… (3) 　　根据试验研究结果,λ值取0.25～0.33为合理的石屑率。已知混合料的密度(一般为2.2～2.3g /cm3