抗裂型水泥稳定碎石基层施工技术要求 　　摘要：水泥稳定碎石初期强度高，并且强度随龄期而增加很快结成板体，因而具有较高的强度，抗渗度和抗冻性较好，施工方法也符合现代化大规模机械化发展的方向，作为路面基层已越来越多的应用到市政建设工程，其涉及的施工作业范围较广，技术性强，本文主要对水稳各阶段技术要求进行了阐述。 　　关键词：水稳施工技术要求抗裂型 　　中图分类号：TU984 文献标识码：A 文章编号： 　　Abstract: the early strength of the cement stable macadam mixture, and the strength increases with age soon formed a plate body, and has high strength, impermeability and frost resistance is good, construction method also conform to the modernization of large-scale mechanization development direction, has been more and more used as pavement base to the municipal construction projects, it involves a wider range of construction work, strong technical, this article mainly expatiates on the stages of water stable technical requirements. 　　Key words: Cement stabilized macadamThe construction technologyrequirements Crack type 　　 　　1水泥稳定碎石作用原理 　　水泥稳定碎石是以级配碎石作骨料，采用一定数量的胶凝材料和足够的灰浆体积填充骨料的空隙，按嵌挤原理摊铺压实。其压实度接近于密实度，强度主要靠碎石间的嵌挤锁结原理，同时有足够的灰浆体积来填充骨料的空隙。它的初期强度高，并且强度随龄期而增加很快结成板体，具有较高的强度，抗渗度和抗冻性较好，施工方法也符合现代化大规模机械化发展的方向。因而在市政工程中的应用会得到很快推广。 　　2原材料技术要求 　　2.1 水泥 　　普通硅酸盐水泥、矿渣硅酸盐水泥、火山灰质硅酸盐水泥都可用于拌制水泥稳定碎石混合料，宜采用强度等级42.5级的缓凝水泥。水泥指标应符合相关标准的规定，见表1。 　　表1水泥质量技术要求 　　 　　 　　采用散装水泥，在水泥进场入罐时，要停放七天，安定性合格后才能使用；夏季高温作业时，水泥入罐温度不能高于50℃，否则，应采用降温措施。 　　2.2 碎石 　　碎石的最大粒径为31.5mm，宜按粒径19~31.5mm、4.75~19mm、2.36mm~4.75mm和0~2.36mm四种规格备料。4号料建议采用坚硬、洁净、无杂质的玄武岩或辉绿岩。集料指标应符合相关标准的规定，见表2～表4。 　　表2水泥稳定碎石粗集料质量技术要求（1#、2#料） 　　 　　 　　表5水泥稳定碎石混合料中合成碎石的颗粒组成 　　 　　 　　凡饮用水皆可使用，遇到可疑水源，应委托有关部门化验鉴定。 　　3混合料组成设计要求 　　3.1 一般要求 　　3.1.1水泥稳定材料的组成设计包括：根据规定的材料指标要求，通过试验选取合适的集料和水泥；确定合理的集料配合比例、水泥剂量、混合料的最佳含水量和相应的最大干密度。合理的水泥稳定碎石组成必须达到强度要求，具有较小的温缩和干缩系数（现场裂缝较少），施工和易性好（粗集料离析较小）。 　　3.1.2振动成型或静压成型水泥稳定碎石7天浸水无侧限抗压强度代表值应满足设计要求。 　　3.1.3为减少基层裂缝，必须做到三个限制：在满足设计强度的基础上限制水泥用量；在减少含泥量的同时，限制细集料、粉料用量；根据施工时气候条件限制含水量。施工中要求水泥剂量不应大于4.5%、合成集料级配中0.075mm以下颗粒含量不宜大于4%、含水量不宜超过最佳含水量的1%。 　　3.2混合料组成设计的步骤 　　3.2.1取工地实际使用的集料，分别进行水洗筛分，按颗粒组成进行计算，确定各种集料的组成比例。要求组成混合料的级配应符合表2的规定。 　　为保证配制出的混合料具有较好的抗裂性能以及施工时减少离析的产生，配合比设计时级配曲线按正“S”形调整。4.75mm以上筛孔通过率宜处于级配中值与上限之间，4.75mm以