淀粉基炭微球的结构及其在电化学电容器中的应用研究化学工艺专业论文.docxVIP

Using potato starch as raw material, through H3PO4 — steam coupling activation method, the starch-based activated carbon microspheres with reasonable porous texture were obtained. The study results showed, with the increase of activation time, the porous texture and mesopore content obviously increased. During the electrochemical test in 6 mol?L-1 KOH, the obtained starch-based activated carbon microspheres showed good electrochemical performance. KEY WORDS： potato starch, carbon microspheres, carbon microstructure, electrochemical performance 目 录 HYPERLINK \l _bookmark0 第一章 文献综述 1 HYPERLINK \l _bookmark1 1.1 炭质材料的结构研究 1 HYPERLINK \l _bookmark2 1.1.1 不同的炭质结构 1 HYPERLINK \l _bookmark3 1.1.2 炭质结构的研究内容与方法 1 HYPERLINK \l _bookmark4 1.1.3 易石墨化炭与难石墨化炭 2 HYPERLINK \l _bookmark5 1.2 生物质炭材料的研究现状 2 HYPERLINK \l _bookmark6 1.2.1 常见生物质炭材料及其前躯体 3 HYPERLINK \l _bookmark7 1.2.2 蔗糖基炭材料 6 HYPERLINK \l _bookmark8 1.3 淀粉及淀粉基炭材料 7 HYPERLINK \l _bookmark9 1.3.1 淀粉及马铃薯淀粉 7 HYPERLINK \l _bookmark10 1.3.2 淀粉基炭材料 8 HYPERLINK \l _bookmark11 1.4 双电层电容器用炭材料 9 HYPERLINK \l _bookmark12 1.4.1 电解质溶液 10 HYPERLINK \l _bookmark13 1.4.2 多孔炭材料 15 HYPERLINK \l _bookmark14 1.4.5 碳纳米管 23 HYPERLINK \l _bookmark15 1.4.6 炭材料表面双电层的形成 27 HYPERLINK \l _bookmark16 1.4.7 赝电容的贡献 30 HYPERLINK \l _bookmark17 1.5 课题的提出及主要研究内容 31 HYPERLINK \l _bookmark18 第二章 淀粉基炭微球的制备及表征手段 33 HYPERLINK \l _bookmark19 2.1 原料和化学试剂 33 HYPERLINK \l _bookmark20 2.1.1 原料来源 33 HYPERLINK \l _bookmark21 2.1.2 原料的物理化学性质 33 HYPERLINK \l _bookmark22 2.1.3 原料的形貌、结构特点 34 HYPERLINK \l _bookmark23 2.1.4 化学试剂 35 HYPERLINK \l _bookmark24 2.2 主要实验仪器和设备 35 HYPERLINK \l _bookmark25 2.3 测试及表征手段 36 HYPERLINK \l _bookmark26 2.4 电化学测试 37 HYPERLINK \l _bookmark27 第三章 无机化学试剂对淀粉基炭微球的促进作用 38 HYPERLINK \l _bookmark28 3.1 实验部分 39 HYPERLINK \l _bookmark29 3.1.1 原料 39 HYPERLINK \l _bookmark30 3.1.2 淀粉基炭微球的制备 39 HYPERLINK \l _bookmark31 3.1.3 材料表征 39 HYPERLINK \l _bookmark32 3.2 无机化学试剂对淀粉稳定化、炭化过程的促进作用 40 HYPERLIN