掺混树脂加工应用-化学工程专业论文.docxVIP

ABSTRACT Blending resin can be divided according to use paste blending resin and battery for blending resin two categories. Paste blending resin accounted for more than 90% mixing resin, Paste blending resin is mainly applied in the field of software products, Battery mixing is mainly used for battery separator belongs to the hard ware. This paper only studies the paste mixed effect of resin on the processing properties of plasticized paste and mixed with the law. The blending resin application has been very mature,The domestic market in the growth stage,According to the experience of foreign countries,Blending resin demand for the demand of about 30% of the volume of paste resin,The blending resin demand is about 150000 tons,While domestic production in 2012 only about 10000 tons, A great potential market.Effect of the blending resin consumption there are many reasons,The main reason is the mixing quality problem of resin products,After the development in recent years, with mixed resin quality has been close to the level of foreign excellent resin,This paper from the aspects of domestic and foreign testing blending resin mixing effect of resin on the plastisol，The main test content：Effects of PB1000, C65V, 75BX on the paste viscosity；Effects of PB1000, C65V, 75BX on the foaming properties of plasticized paste；Effects of PB1000, C65V, 75BX on the mechanical properties of plasticized paste. Through a lot of experiments summarized the effects of mixing processing properties of the resin（PB1000、C65V、75BX） for paste resin. And summarize the relevant rules are as follows,The plastisol viscosity greatly reduced,Add the larger proportion of the lower viscosity,To improve the surface gloss products and hand,Reduce the tensile strength of the product,At the same time, experiments have proved that the blending resin quality and reach the international level of blending resin. KEY WORDS: Blending resin,pvc, Paste resin, plastisol, mechanical behavior I I 目 录 第一章 前言 1 第二