浅述渠道伸缩缝施工工艺 　　【摘 要】渠道伸缩缝填料及其施工工艺，是渠道防渗中必须解决的问题。实际工程中，对渠道已铺衬土工膜的，以求节省费用，对铺衬土工膜，有的采用沥青砂浆、焦油朔料胶泥进行灌缝处理。这种材料受气温影响，温度高表面壅起，温度低脆裂，易老化且不环保；由于裂缝易导致渠道渗透破坏，需尝试采用新的材料和新的施工方法进行防渗。?? 　　【关键词】渠道伸缩缝；聚氨酯砂浆；防渗 　　Discuss construction technology of channel expansion joint?? 　　Liu tao?? 　　(Xinjiang Tarim Basin Authority Bureau Service Center Korla Xinjiang 841000) ?? 　　【Abstract】The channel expansion joint filler and its construction technology, is to be anti-seepage problems. The actual project, on the channels Shop geomembrane liner in order to save costs, on the Shop geomembrane liner, and some use of asphalt mortar, tar plastics processing clay for irrigation joints. This material affected by the temperature, the temperature high surface obstruct, the temperature low rattle, aging is not easy to environmental protection; as a result of the cracks easily lead to the infiltration and sabotage channels need to try new materials and new construction methods for anti-seepage.?? 　　【Key words】Channel expansion joints; Polyurethane mortar; Seepage 　　1. 工程概况?? 　　某工程渠线全长168.8Km，属大（Ⅰ）型Ⅰ等工程，工程主要由渠首分水枢纽、输水明渠、无压输水隧洞，分水闸、节制退水闸，输水渡槽，排洪渡槽，排洪涵洞，交通桥等建筑物组成。?? 　　根据该工程设计结构，渠道长19.955m为一个隔梁段，一个隔梁段有四道垂直渠道断面的伸缩缝，伸缩缝长度沿隔梁边和渠道衬砌板边布置，伸缩缝的宽度为20mm，缝深60mm；干渠伸缩缝所采用的灌注材料按重量比4：6现场拌制的聚胺脂砂浆；在防渗渠道是梯形断面的情况下，聚氨酯砂浆灌注渠坡缝内使其达到设计要求，也不是一件容易的事；根据伸缩缝的断面结构，气温条件下，水平缝聚氨酯砂浆选用自流型，斜坡缝聚氨酯砂浆选用非下垂型。?? 　　2. 伸缩缝处理的几种型式?? 　　2.1 沥青砂浆填缝。 　　填缝材料采用1：1：4（沥青：水泥：砂）沥青砂浆，施工时先将沥青加热至140～170℃，水泥和砂分别加热至160℃，将沥青、水泥和砂按比例装入容器内搅拌均匀，至颜色一致。在灌注沥青砂浆前先将伸缩缝内清理干净，灌注温度不低于110℃，待温度降低后用勾缝刀压实抹光。该法在经济投入上相对较省，但材料不环保，夏季高温施工时易流淌，受温度影响易老化。?? 　　2.2 焦油塑料胶泥填缝。 　　焦油朔料胶泥配比按煤焦油：聚氯乙烯薄膜：癸二酸二辛酯 ：粉煤灰=100:15:2:30配制。该法在经济投入上最省，采用废旧朔膜作为填料熬制，材料杂质较多，随坡流淌，渠坡灌缝困难，夏季胶泥表面易壅起，冬季易脆裂。?? 　　2.3 聚氨酯砂浆填缝。 　　聚氨酯砂浆作为新型的材料，用于伸缩缝灌缝材料，施工简便，课低温操作，高温不流淌，低温不脆裂，-3 ℃有较好的弹性，无毒无害，耐老化性能好，在实际施工中经试验后效果很好，但原材料价格较高。?? 　　表1 伸缩缝采用的施工方法 　　 　　施工方法 具体做法 使用条件 　　冷?で丢し? 批?す为し? 密封材料不需加热，手工嵌填时可用腻子刀或刮刀先将密封材料批刮到缝槽两侧的粘接面，然后将密封材料填满整个接缝 适用于平面或立面接缝的密封处理 　　 挤?こ霆し?可采用专用的挤出枪，并根据接缝宽度选用合适的枪嘴，将密封材料挤入接缝内 适用于平面或立面接缝的