酚醛树脂基氧化镁模板炭的制备及其在超级电容器中的应用化学工艺专业论文.docxVIP

capacitance of 221 F·g-1 at a current density of 50 mA·g-1, and carbon MCPF(R)82 got the capacitance of 186.8 F·g-1. Besides, the rate performances of the two carbon systems were found to be following the same trend with mesopore ratio. The two parameters both increased firstly then decreased with growing MgO:PF mass ratio. The carbons MCPF(N)46 and MCPF(R)73 got the rate performance of 98.3 % and 89.4%, individually, expressed as the ratio of the capacitance measured at 1000 mA·g-1 against that at 50 mA·g-1. KEY WORDS：supercapacitor, electrochemical performance, template, mesoporous carbon, pore structure 目 录 HYPERLINK \l _bookmark0 前 言 1 HYPERLINK \l _bookmark1 第一章 文献综述 2 HYPERLINK \l _bookmark2 1.1 多孔炭 2 HYPERLINK \l _bookmark3 1.1.1 多孔炭的微观结构 2 HYPERLINK \l _bookmark4 1.1.2 多孔炭的制备方法 4 HYPERLINK \l _bookmark5 1.1.3 模板法制备多孔炭材料 8 HYPERLINK \l _bookmark6 1.1.4 多孔炭的性质及应用 14 HYPERLINK \l _bookmark7 1.1.5 多孔炭材料的表征 14 HYPERLINK \l _bookmark8 1.2 超级电容器 17 HYPERLINK \l _bookmark9 1.2.1 超级电容器的分类及工作原理 18 HYPERLINK \l _bookmark10 1.2.2 超级电容器的结构 21 HYPERLINK \l _bookmark11 1.3 多孔炭材料结构与超级电容器性能的关系 22 HYPERLINK \l _bookmark12 1.3.1 比表面积 22 HYPERLINK \l _bookmark13 1.3.2 孔径分布 22 HYPERLINK \l _bookmark14 1.3.3 表面官能团 23 HYPERLINK \l _bookmark15 1.3.4 内阻 23 HYPERLINK \l _bookmark16 1.4 论文选题的意义及主要研究内容 24 HYPERLINK \l _bookmark17 第二章 酚醛树脂基 MgO 模板炭的制备和表征方法 25 HYPERLINK \l _bookmark18 2.1 实验原料、化学试剂及设备仪器 25 HYPERLINK \l _bookmark19 2.1.1 原料来源及性能参数 25 HYPERLINK \l _bookmark20 2.1.2 主要化学试剂 25 HYPERLINK \l _bookmark21 2.1.3 主要仪器与设备 26 HYPERLINK \l _bookmark22 2.2 MgO 模板炭的制备方法 27 HYPERLINK \l _bookmark23 2.3 多孔炭材料的表征方法 29 HYPERLINK \l _bookmark24 2.3.1 透射电镜(TEM)分析 29 HYPERLINK \l _bookmark25 2.3.2 X 射线衍射(XRD)分析 29 HYPERLINK \l _bookmark26 2.3.3 热失重(TGA)分析 29 HYPERLINK \l _bookmark27 2.3.4 低温氮气吸脱附分析 29 HYPERLINK \l _bookmark28 2.4 电容器组装及其电化学性能测试分析 30 HYPERLINK \l _bookmark29 2.4.1 炭电极的制备 30 HYPERLINK \l _bookmark30 2.4.2 双电层电容器的结构与组装 30 HYPERLIN