高强度高精密电子印刷聚酯丝网的强力与粘结性能提升-纺织工程专业论文.docxVIP

万方数据 万方数据 高强度高精密电子印刷丝网的强力与粘结性能提升 Secondly, the cleaning process of oligomer on the screen surface is studied, the final selections of process are as follows: (1) ultrasonic alkali collaborative process that is: NaHCO3/Na2CO3 (1:1,w/w) concentration of 10g/l，bath ratio of 50:1, oil bath at 130 ℃ for 35min, ultrasonic wave with 15min; (2) adding surfactant. The specific process is: the compound additive 5g/l, bath ratio of 50:1, mixed additives: chloroform, LAS (twelve sodium dodecyl benzene sulfonate), Tx-100 (octylphenol ethoxylates) quality ratio of 1:1:1(w/w/w). 3. Study on surface roughening of polyester mesh The polyester mesh of alkali treatment, plasma treatment, and the use of net grinding paste treatment is studied in order to improve photographic glue binding capacity. Plasma processing conditions are determined as: reactive power of 110 W, reaction time 80s, plate distance is 3.9mm, vacuum degree was -0.4bar. Strength loss value can be controlled within 5%. Alkali treatment and grinding paste treatment while coarsening screen surface play a positive role, but the screen strength decreased more seriously. If the screen printing is to build a skyscraper, net frame is the buildings skeleton, then, the screen is the buildings foundation, mesh quality decides screen printing quality and height in a certain extent. We still have a lot to improve the quality and performance of the screen, to improve its strength and combine with the photosensitive adhesive easily, prevent the phenomenon of misregiste, etc, so that the electronic printing technology will create greater economic value in the future. Yang Xiaohui（Textile Engineering (Dyeing and Finishing) Supervised by Associate Prof. Ge Fengyan KEY WORDS: polyester mesh, heat setting, oligomer cleaning, alkali treatment, plasma treatment V 高强度高精 高强度高精密电子印刷丝网的强力与粘结性能提升 目 录 摘 要 .......................................................................................................................... I ABSTRACT......