连续纤维增强热塑性复合材料浸渍模拟及优化研究-动力工程及工程热物理专业论文.docxVIP

优秀毕业论文 精品参考文献资料 北京化工大学硕士学位论文黏度升高、浸渍辊半径减小，楔形区内熔体对纤维束的浸渍效率降低：纤 北京化工大学硕士学位论文 黏度升高、浸渍辊半径减小，楔形区内熔体对纤维束的浸渍效率降低：纤 维束的浸渍程度随着牵引速度的降低，加工温度的升高，浸渍辊数的增加 而增大；浸渍辊半径增大，辊间距减小可以增大纤维束和浸渍辊之间的包 覆角，使纤维束分散展宽变大，从而有利于提升纤维束的浸渍程度。 为了提升树脂对纤维的浸润性，提高纤维和树脂之间的界面结合强度， 本文利用纳米SiO：颗粒修饰玻璃纤维表面，协调PP—g—MAH的增容作用， 有效改善了纤维和树脂之间的界面结合，明显提高了复合材料的力学性能。 改性后复合材料的孔隙率降低了59．88％，层间剪切强度提高了116．06％， 拉伸强度提高了109．14％，弯曲强度提高了99．85％，冲击强度提高了 1】6．70％。 关键词：连续纤维，热塑性复合材料，浸渍模拟，楔形区压力，浸渍程度， 界面结合优化 万方数据 IMPREGNATIoN IMPREGNATIoN SIMULATIoN AND oPTⅡ讧IZATION STUDY oF CoNTINUoUS FIBER REINFoRCED THERMoPLASTIC CoMPoSITE MATERIALS ABSTRACT Melt impregnation process is one of the mainstream technology for manufacturing continuous fiber reinforced thermoplastic composites at home and abroad now,the main difficulty of this process is how to make the resin with high viscosity infiltrated into the fiber bundle well，and achieve a good combination between the fiber and resin．To solve this problem，a lot of researches about impregnating simulation and optimization of the process had been made at home and abroad，and the wedge areas between the pins and fiber,which have become major research focus，are recognized as the key areas to achieve driving force make melt impregnated into the fiber bundle． However,due to the feature of¨black box¨in the region，most of researches were combined with more empirical formula indirect modeling studies，which could’t accurately describe the relationship between the region and the impregnation degree of fiber bundle． This paper used the melt impregnation equipment developed independently,combined with experimental design methods to make preliminary experimental study of melt impregnation process of continuous 万方数据 北京化工大学硕士学位论文glass 北京化工大学硕士学位论文 glass舶er reinforced polypropylene composites，and established an empirical model of relationship between main process parameters(processing temperature，pulling speed，pin numbers)and impregnation degree of fiber bundle． Combined Reynolds equation with Darcy’S law to establish t