东北林业大学理学院）宋永明王清文（生物质材料科学与技术-BOKU.pptVIP

Thank you for your attention！ * Effects of APP on the Fire-retardant and Mechanical properties of Wood-flour/HDPE Composite WANG Qing-Wen, SHAO Bo, ZHANG Zhi-Jun, SONG Yong-Ming Northeast Forestry University, Harbin, China IUFRO D5 Conference 2007, Taipei 1 Introduction Background of this Research ? WPC industry is growing fast Production of WPC in China mainland: 200 000 – 250 000 t/a, 2006 5 000 – 10 000 t/a, 2001 WPC in Olympic Park, Beijing 1 Introduction Background of this Research ? Interior application of WPC is promising WPC almost releases no VOCs WPC is a good way to use the wastes of wood processing WPC is excellent in dimensional stability concerning moisture WPC is environment friendly Northeast Forestry University, Harbin, China 1 Introduction Background of this Research ? The fire of WPC is more destructive than wood fire Polyolefin-based WPC: The HRR is at least 2 times the value of wood PVC-based WPC: The smoke generation is much heavier than wood The smoke is very corrosive to metals Northeast Forestry University, Harbin, China 1 Introduction Background of this Research ? Research of fire retardant WPC is demanding No fire retardants are effective for both of wood and plastic Effective fire retardants for polyolefin are either containing halogen element or need high loading ? Opportunities for fire retardant WPCs of high wood content (e.g. WF-HDPE) Use effective fire retardants for wood with higher loading Create new fire retardants for plastics Northeast Forestry University, Harbin, China 2 Experimental 2.1 Materials and apparatus High density polyethylene (HDPE), 2200J; Poplar wood flour (WF), 40-80mesh; Paraffi