含气量对再生混凝土力学性能及抗冻性影响试验研究结构工程专业论文.docxVIP

哈尔滨工业大学工学硕士学位论文 哈尔滨工业大学工学硕士学位论文 哈尔滨工业大学工学硕士学位论文 哈尔滨工业大学工学硕士学位论文 - - II - - - III - Abstract With the rapidly development of construction industry, more and more concrete was consumed. This caused lots of problems, such as the aggregate resource scarcity, land occupied by waste concret, environmental pollution and so on. The emergence of recycled concrete technology, effectively resolved the contradictions, and ensured the sustainable development in the industry, which has an industrializational development prospects. In China, at present the study about durability of recycled concrete is less, especially in anti-freeze durability aspect, different scholars have different conclusion. In order to expand the application range of the recycled concreteI chose recycled concrete’s basic mechanical properties and anti-freeze capability as the main research direction, to study the impact of Air-entraining agent to recycled concrete. In order to research the effect of the attached mortar of recycled aggregate on properties of recycled concrete, original mortar was produced with air entrainment of 1.5% ,3%, 5%, 7%. This paper studied the influence of air entrainment to original mortar’s cube and prism compressive strength, splitting tensile strength, bending strength and dry shrinkage. The results showed that, with the increase of air entrainment, the mortar’s strength decreased and the shrinkage increased. The above original mortar was made into recycled coarse aggregate by crushing and screening. Technical indexes of recycled coarse aggregate were investigated according to Recycled Aggregate for Concrete ( HYPERLINK /tushumulu/353349/ GB/T25177-2010). The test results showed that the recycled coarse aggregate was class III. Recycled concret was producted by different air entrainment recycled aggregate. By means of quick freeing and thawing test, compared with ordinary concrete, the freezing and thawing resistance of air-entrained concret when diff