c868-85中文版-防护衬里耐化学侵蚀性试验方法标准.docVIP

C 871 PAGE 399 Designation: C 868 - 85 (Reapproved 1995)ε1 编号：C 868 - 85（1995年重新获批）1 PAGE 398 Standard Test Method forChemical Resistance of Protective Linings This test method is under the jurisdiction of ASTM Committee C-3 on Chemical-Resistant Nonmetallic Materials and is the direct responsibility of Subcommittee C03.01 on Test Methods.本试验方法由ASTM委员会C-3耐化学侵蚀非金属材料委员会管辖，并 This test method is under the jurisdiction of ASTM Committee C-3 on Chemical-Resistant Nonmetallic Materials and is the direct responsibility of Subcommittee C03.01 on Test Methods.本试验方法由ASTM委员会C-3耐化学侵蚀非金属材料委员会管辖，并由C03.01试验方法分委会直接负责。 Current edition approved Aug. 30, 1985. Published October 1985. Originally published as C 868 - 77. Last previous edition C 868 - 77.现行版本于1985年8月30日批准，并于1985年10月出版。最初以C868 – 77编号出版。上一版本编号为C 868 – 77。 This standard is issued under the fixed designation C 868; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (ε) indicates an editorial change since the last revision or reapproval.本标准以固定编号C 506刊发；紧随编号后的数字表示最初采用的年份，或者是修订版的最后修订年份。圆括号中的数字表示最新重新批准的年份。上标(ε)表示自上一修订版或重新批准后所作的编辑性修改。 ε1 Note—The safety caveat was updated and Keywords were added in September 1995.ε1 注——于1995年9月更新了安全警告并增加了关键词。 1. Scope 适用范围 1.1 This test method covers a procedure for evaluating the chemical resistance of a protective lining applied to a steel substrate. The method closely approximates the service conditions, including the temperature differential between the external and internal surfaces of the equipment, which may accelerate permeation of the lining by a corrosive media. This test method may be used to simulate actual field use conditions insofar as a qualitative evaluation of the lining system after a predetermined period of exposure.本试验方法涵盖了评估运用在钢铁基底上的防护内衬的耐化学侵蚀性程序。本方法非常接近使用条件，其中包括设备外部和内部表面之间的、通过腐蚀性介质可能加速