c905-96中文版-抗化学腐蚀灰浆、薄泥浆、整体面层和聚合物混凝土的表观密度的标准试验方法.docVIP

C 905 PAGE 597 Designation: C 905 - 96 编号：C 905-96 PAGE 590 Standard Test Methods forApparent Density of Chemical-Resistant Mortars, Grouts,Monolithic Surfacings, and Polymer Concretes These test methods are under the jurisdiction of ASTM Committee C-3 on Chemical-Resistant Nonmetallic Materials and are the direct responsibility of Subcommittee C03.01 on Test Methods. These test methods are under the jurisdiction of ASTM Committee C-3 on Chemical-Resistant Nonmetallic Materials and are the direct responsibility of Subcommittee C03.01 on Test Methods.这些试验方法归ASTM委员会C-3耐化学侵蚀性非金属材料委员会管辖，并由C03.01试验方法分委会直接负责。 Current edition approved Sept. 10, 1996. Published November 1996. Originally published as C 905 - 79. Last previous edition C 905 - 85(1990).现行版本于1996年9月10日批准，并于1996年11月出版。最初版本编号为C905-79，上一版本编号为C 905-85（1990）。 抗化学腐蚀灰浆、薄泥浆、整体面层和聚合物混凝土的表观密度的标准试验方法1 This standard is issued under the fixed designation C 905; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (ε) indicates an editorial change since the last revision or reapproval.本标准以固定编号C 905刊发；紧随编号后的数字表示最初采用的年份，或者是修订版的最后修订年份。圆括号中的数字表示最新重新批准的年份。上标(ε)表示自上一修订版或重新批准后的编辑性修改。 1. Scope 适用范围 1.1 These test methods cover the procedures for determining the uncured (wet) and conditioned (dry) densities of resin, silicate, silica, and sulfur-based chemical-resistant mortars, grouts, monolithic surfacings, and polymer concretes.这些试验方法涵盖测定以树脂、硅酸盐、二氧化硅、硫磺为基本成分的抗化学侵蚀灰浆、薄泥浆、整体面层和聚合物混凝土的未硬化（湿）密度和硬化（干）密度的程序。 1.2 Density Method I: Apparent Uncured Density of Resin, Silica, and Silicate Materials—This test method is not applicable to sulfur materials.密度测定方法I：树脂、二氧化硅、硅酸盐材料的表面未硬化密度——本试验方法不适用于含硫材料。 1.3 Density Method II: Apparent Conditioned Density of Resin and Sulfur-based Materials—This test method may be applicable to silica or silicate materials if