c948-81中文版-玻璃纤维增强混凝土薄片的干和湿体积密度、吸水率和表观孔隙率的标准试验方法.docVIP

C 948 PAGE 630 Designation: C 948 - 81 (Reapproved 1994)编号：C 948 - 81（1994年重新审批） PAGE 629 Standard Test Method for Dry and Wet Bulk Density, Water Absorption, and Apparent Porosity of Thin Sections of Glass-Fiber Reinforced Concrete This test method is under the jurisdiction of ASTM Committee C-27 on Precast Concrete Products and is the direct responsibility of Subcommittee C27.40 on Glass Fiber Reinforced Concrete Made by the Spray-Up Process.本规范由ASTM委员会C-27预制混凝土制品委员会管辖，并由C27.40喷射成形制造的玻璃纤维增强混凝土 This test method is under the jurisdiction of ASTM Committee C-27 on Precast Concrete Products and is the direct responsibility of Subcommittee C27.40 on Glass Fiber Reinforced Concrete Made by the Spray-Up Process.本规范由ASTM委员会C-27预制混凝土制品委员会管辖，并由C27.40喷射成形制造的玻璃纤维增强混凝土分委会直接负责。Current edition approved June 8, 1981. Published August 1981.现行版本于1981年6月8日批准，并于 This standard is issued under the fixed designation C 948; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (ε) indicates an editorial change since the last revision or reapproval.本标准以固定编号C 948刊发；紧随编号后的数字表示最初采用的年份，或者是修订版的最后修订年份。圆括号中的数字表示最新重新批准的年份。上标(ε)表示自上一修订版或重新批准后的编辑性修改。 1. Scope适用范围 1.1 This test method covers the determinations of dry and wet bulk density, water absorption, and apparent porosity of thin sections of glass-fiber reinforced concrete.本试验方法涵盖玻璃纤维增强混凝土薄片的干和湿体积密度、吸水率和表观孔隙率的测定。 Note 1—This method does not involve a determination of absolute specific gravity. Therefore, such pore space as may be present in the specimen that is not emptied during the specified drying or is not filled with water during the specified immersion is considered impermeable and is not differentiated from the solid portion of the specimen for the calculations, especially those for percent voids.注1——本方法未包含绝对比重的测定。因此，规定干燥期间不能清空或规定浸渍期间不得填充水的试样里出现的孔