浅析电炉石墨电极耗损的原因及控制措施(杨光).pdfVIP

浅析电炉石墨电极耗损的原因及控制措施 1 杨 光 ；袁海滨；熊银宝 （云南锡业股份有限公司铜业分公司，云南个旧市，661000 ） 摘要：本文简要研究了电炉石墨电极的耗损原因，研究结果表明， 电极的额外耗损量远远超过了其实际使用量， 电极的侧面氧化 电极 的折断占了很大的比例。本论文就如何通过改变操作方式来降低石墨 电极消耗做了研究。 关键词 ：石墨电极;侧面氧化;折断耗损;热剥落 Discussion the Reason on the Electric furnace Graphite electrode Consumption and Control measures YANG Guang ，YUAN Hai-bin ，XIONG Yin-bao (Copper branch of Yunnan Tin Group Limited Company, Yunnan Gejiu, 661000, China) Abstract: The consumption reasons on the electric furnace graphite electrode have been analyzed. The results show that additional loss of graphite electrode is further beyond than its real usage, because the graphite electrode of side oxidation and electrode break accounted for a large proportion. Control measures for reduce the consumption of graphite electrode by change operation mode have been analyzed. 1作者简介：杨光（1988-），男，冶炼技术员，云南建水人，主要从事 有色冶炼技术工作 Keywords: Graphite electrode; Side oxidation; Electrode break; Thermal spalling 1 引言 石墨电极耗损是主要制约电炉生产成本的一个关键因素，对于研 究降低石墨电极耗损不仅可以实现低投入高产出，更重要的是能产生 巨大的社会效益，响应国家低碳环保的号召。 目前我厂的电炉使用的是高功率石墨 电极，经过统计，电极单耗 在 2.5kg∕ t 铜锍，而其同行业的电极单耗大约在 1.2kg∕ t 铜锍。相比同行 业我厂的电极单耗明显偏高，所以对于降低石墨电极消耗对我厂在节 能降耗、降低生产成本方面来说是十分重要的。 2 影响石墨 电极耗损的原因 2.1 石墨电极的特性 石墨 电极是将石油焦等骨料和沥青等粘结剂混合在一起压型成 规定的形状，经焙烧、浸渍、石墨化等工序处理后，再经机械加工而成。 电炉采用石墨电极作为发热体是由于它耐高温、加工容易、价格便宜。 而且它有较高的电阻，且随温度的变化不大，在 2500℃以下石墨电极 的机械强度随温度的上升而提高，可作为在加热体断面积较大的情况 下采用低电压高电流的 电源，固都采用石墨 电极作为电炉的加热体。 2.2 石墨电极易损的原因分析 2.2.1 侧面损耗 电极侧面耗损，主要是由于炉膛存在有负压，进而炉内有大量的 流动空气，空气中的氧与石墨作用生成 CO CO ，氧化时的生成物 2 随环境温度的不同而不同： 2C+O =2CO （1000℃以上）