放电等离子烧结TiB_(2)-B_(4)C复相陶瓷材料的力学性能和微观组织.pdfVIP

・42・ 2023年第2期 放电等离子烧结TiB2-B4C复相 晦瓷材料的力学性能和微观组织 张超 (西安工业大学机电工程学院，西安 710021) 摘 要：采用放电等离子烧结技术制备了 TiB2-B4C复相陶瓷材料，研究了烧结温度和保温时间对TiB2-B4C 陶瓷刀具材料力学性能和微观组织的影响 。研究表明 ，当烧结温度为1700°C ,保温5 min时，陶瓷刀具材料的微观 组织均匀，晶粒相对细小，致密度较高，材料的组织缺陷最少，综合力学性能较优 。此时，抗弯强度598MPa,硬度 22. 8GPa,断裂韧性约为 6. 8MPa • m1/2 o 关键词:SPS烧结；力学性能；微观组织；烧结工艺 中图分类号:TG711 文献标识码：A 文章编号：1674-957X(2023)02-0042-03 Mechanical Properties and Microstructur of Spark Plasma Sintered TiB2-B4C Composites Zhang Chao (School of Mechatronic Engineering, Xian Technological university, Xi,an 710021, China) Abstract: TiB2 -B4 C multiphase ceramic materials were prepared by spark plasma sintering. The effects of sintering temperature and holding time on the mechanical properties and microstructure of TiB2-B4C ceramic tool materials were studied. The results show tha when the sintering temperature is 1700 °C and the holding time is 5min, the microstructure of the ceramic tool material is uniform, the grains are relatively small, the density is high, the structural defects of the material are minimum, and the comprehensive mechanical properties are be ­ ter ・ A this time, the bending strength is 598MPa, the hardness is 22. 8GPa, and the fracture toughness is abou 6. 8MPa ・ m1/2. Key words :Spark plasma sintering； Mechanical properties；microstructure； Sintering process 1引言 探讨宏观尺度下力学性能和微观组织间的联系。 陶瓷刀具在高速切削加工过程中会受到机械冲击和 2实验方法 热冲击的双重作用，因此陶瓷刀具材料在常温和高温下都 2.1材料制备 需具备良好的力学性能3」 。TiB2具有高强度和高硬度， 实验所需材料均釆购于秦皇岛一诺高新材料开发有 优异的热力学稳定性和化学稳定性，是一种优良的陶瓷刀 限公司，商品TiBa （纯度99.5%,粒径（0. 5 — lfjimjB/C 具候选材料 。但TiB?具有较强的共价键,较低的自扩散 （纯度99%,粒径0. 5Mm）粉体为主要原料