液相法制备超细、纳米Co3O4粉末及其性能表征的中期报告.docxVIP

液相法制备超细、纳米Co3O4粉末及其性能表征的中期报告 摘要： 本文利用液相法在室温下制备了一种纳米级的Co3O4粉末，并对其进行了性能表征。通过红外光谱（IR）、X射线粉末衍射（XRD）、透射电子显微镜（TEM）和氮气吸附-脱附（BET）等技术对Co3O4粉末进行了表征。结果表明，所制备的Co3O4粉末平均粒径为16.52 nm，具有很强的晶体结构和热稳定性。此外，所制备的Co3O4粉末具有高比表面积和孔隙结构，表明其在催化、电化学等方面具有较好的应用潜力。 关键词：液相法；Co3O4粉末；纳米级；性能表征；应用潜力。 Abstract: In this study, a nanoscale Co3O4powder was prepared by the liquid-phase method at room temperature, and its properties were characterized. Co3O4 powder was characterized by infrared spectroscopy (IR), X-ray powder diffraction (XRD), transmission electron microscopy (TEM) and nitrogen adsorption-desorption (BET). The results showed that the average particle size of the prepared Co3O4powder was 16.52 nm, which had strong crystal structure and thermal stability. In addition, the prepared Co3O4 powder had high specific surface area and pore structure, indicating its potential for application in catalysis, electrochemistry and other fields. Keywords: Liquid-phase method; Co3O4 powder; Nanoscale; Property characterization; Application potential.