Glare层板基本成形性能研究与实验验证.docx

Glare层板根本成形性能争论与试验验证

田精明;李华冠;刘成;陶刚;张丽清;郑兴伟;刘红兵;陶杰

【摘要】为了探究Glare层板的成形性能特点,承受单向拉伸试验和三点弯曲试验,分析争论了Glare2A,Glare2B和Glare3层板的根本成形性能,并借助扫描电子显微镜分析了Glare层板的失效特征。结果说明：纤维铺层方向对材料的成形性能存在显著影响,Glare2A层板抵抗塑性变形的力量强,且难以发生厚向变形：承受σ=σy+Kεn硬化模型拟合真实应力-应变曲线,其相关系数最大,拟合结果最好：Glare2A的弯曲回弹量最大,其弯曲破坏时,内表层受压应力,以皱缩和压缩断裂为主,外表层受拉应力,以纤维拉伸断裂和分层为主；对于Glare2B层板,其弯曲回弹量最小,主要以基体破坏为主：通过滚弯成形验证了试验所得结果的准确性。%ThebasicformabilityofGlare2A,Glare2BandGlare3laminateswasinvestigatedbyunidirectionaltensileandthree-pointbendingteststoexploretheformabilitycharacteristicsofGlare.Meanwhile,thefailurecharacteristicofGlarewasstudiedbyscanningelectronmicroscopy

(SEM).TheresultsindicatethatthedirectionofthefiberhasstrongeffectsontheformabilityofGlare.TheGlare2Alaminatesexhibitthestrongestresistancetoplasticdeformation.Meanwhile,itisalsohardtodeforminthicknessdirection.σ=σy+Kεnisusedtofittherealstress-straincurvesofthreevariantsandprovesthemostsuitablemodel,presentingthemaximumcorrela-tioncoefficient.Furthermore,Glare2Alaminatesexhibitthemostseriousbendingspringback.Shrinkageandcompressionfracturearevisibleintheinnerlayerwhichbearscompressivestress,andfiberfractureanddelaminationarefoundintheouterlayer

whichbearstensilestress.Onthecontrary,Glare2Blaminatesshowthe

minimumspringback,followingwiththeobservedfiber-matrixcracks.Fi-nally,theaccuracyoftestresultsisverifiedbyrollbending.

【期刊名称】《航空材料学报》

【年(卷),期】2023(037)001

【总页数】7页(P86-92)

【关键词】复合材料;Glare层板;根本成形性能;硬化模型;回弹

【作者】田精明;李华冠;刘成;陶刚;张丽清;郑兴伟;刘红兵;陶杰

【作者单位】南京航空航天大学材料科学与技术学院，南京211106;南京航空航天大学材料科学与技术学院，南京211106;南京航空航天大学材料科学与技术学院，南京211106;南京航空航天大学材料科学与技术学院，南京211106;南京航空航天大学材料科学与技术学院，南京211106;上海飞机制造，上海202336;上海飞机制造，上海202336;南京航空航天大学材料科学与技术学院，南京211106

【正文语种】中文

【中图分类】TB333

纤维金属层板(FiberMetalLaminates，FMLs)是一种由金属薄板和纤维复合材料交替铺层后，在肯定的固化工艺下制备而成的层间混杂复合材料。FMLs具有高比刚度和比强度的特点，并且拥有优良的疲乏性能