功能合成纤维.pptx

功能合成纤维Syntheticfiber

Melt,Wet,DrySpinning 湿式纺丝加工流程干式纺丝加工流程I7熔融纺丝加工流程抽丝影片

Dry-JetWetSpinning,Meltblown 干喷湿纺加工流程熔喷(Meltblown)加工流程18

合成纤维假捻加工与制棉织造Weaving/Knitting织造Weaving/Knitting制棉加工StapleProcess牵切加工TowforSliver加工丝织物TexturedFabric丝状纤维织物FilamentFabric棉状织物StapleFabricSpunFabric梳毛纱织物WorstedFabric棉状纱StapleYarnSpunYarn梳毛纱WorstedYarnStaple丝束Tow聚合体PolymerFilament部分延伸丝PartiallyOrientedYarnPOY混纺Blending,(E/W,E/C,E/R)未延伸丝UndrawnYarnUDY卷缩加工丝TexturedYarnDTY混纺(Blending)Spinning,E/C,E/R织造Weaving/Knitting织造Weaving/Knitting卷缩加工TexturingYarn延伸假捻加工Draw-Texturing伸捻加工Draw-Twisting完全延伸丝FullyOriented熔融纺丝MeltSpinning棉状纤维StapleFiber毛条TopFOY/HOY19

?TY(TexturedYarn)：是由纺丝卷绕-拉伸加捻-假捻变形的三步法工艺制得的丝或是由高速纺丝-低速假捻工艺制得的丝.其具有一定的弹性和蓬松性.尺寸稳定性较好?DTY(DrawTexturedYarn)利用POY做原丝.进行拉伸和假捻变形加工.纤维是卷曲的。具一定的弹性及收缩性.剩余伸长一般在40%以上.比较稳定?ATY(Air-TexturedYarn)美国杜邦发明.原理是利用喷气法使空气喷射技术对丝束进行交络加工.形成不规则扭结丝圈.使丝束具有蓬松毛圈状的纱。加工成的变形纱兼有长丝和短纤纱两者的性能.毛感强.手感好.覆盖性优于短纤纱。?CationicDyeableDrawTexturedYarn(阳离子染色加工丝)?BCF(BulkedContinuousFilament)：NylonyarnforCarpet?PolyesterStapleFiber(PSF)?PolyesterFilamentYarn(PFY)?UDY(UndrawYarn)1000-1500m/min?MOY半预取向丝（中速纺丝）：其纤维分子已有少量取向.取向度高于UDY.低于预取向丝.这种丝的结构状态仍然不够稳定.不能直接应用?POY(Pre-orientedYarn/PartiallyOrientedYarn)部分延伸丝：因分子结构不稳定.经长期存放后.大分子的结晶、顺向会发生变化.进而会影响DTY染色差异.3000-3500m/min。?FOY(FullyOrientedYarn)/：经纺嘴后将其伸度拉至约3%以下且不再做变形加工.外观平滑无膨松状各纤维之间密合度相当高.一般断面呈圆形(若纺嘴形状非圆形则视纺嘴形状而有不同形状).透气性差.手感较硬(相对于DTY).衣着类一般使用其仿丝绸特性纤维已充分拉伸.纤维是直的.可直接用于织布工程HOY高取向丝（超高速纺丝）：5000-6000m/min?FDY(FullDrawYarn)全延伸丝：低速纺丝、高速拉伸且兩道工序在一台紡絲拉伸联合机上完成 专业名词

?一般制程下的ATY是利用空气喷射气流.将主纱的纤维分离、松弛、弯曲.形成不规则毛圈.进而排列密集、互相交缠.并包覆配纱（弹性纱线）.形成组织结构紧密.但有短纤外观手感的化纤纱线ATY

变形丝(缔卷加工丝