回火对低碳贝氏体钢组织与性能的影响.pdfVIP

回火对低碳贝氏体钢组织与性能的影响 赵 慧 王学敏 张小帆 郑超超 高 磊 （北京科技大学，材料科学与工程学院，北京 100083 ） 摘 要 利用扫描电镜( SEM )，电子背散射衍射分析技术(EBSD)，X 射线衍射(XRD)研究不同回火温度对低碳贝 氏体钢组织和性能的影响。结果表明，回火温度对试验钢的屈服强度和伸长率的影响更为明显，而对抗拉强度的影 响相对较小；未经回火时，试验钢的轧态组织为细小的板条贝氏体和M/A 岛，随着回火温度的增加，贝氏体板条 逐渐合并在一起，680℃回火1h 后产生大量残余奥氏体，可获得良好的综合力学性能。 关键词 低碳贝氏体钢 回火 残余奥氏体 力学性能 Effect of Tempering on Microstructure and Mechanical Properties of Low Carbon Bainitic Steel Zhao Hui Wang Xuemin Zhang Xiaofan Zheng Chaochao Gao Lei (School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing, 100083) Abstract Effect of different tempering temperatures on microstructure and properties of Low Carbon Bainitic Steel was investigated by scanning electron microscopy (SEM), electron back scatter diffraction(EBSD),and X-Ray Diffraction(XRD).The results show that tempering temperature has considerable influence on yield strength and the elongation of the steel, but the influence on the tensile strength is not obvious. The main microstructure in the steel is lath bainite and M/A before tempering. With increasing the tempering temperatures, the bainitic lath can gradually merge. the microstructure generates a larger number of retained austenite after tempering at 680 ℃ for 1 hour, the test steel plate can gain favorable comprehensive mechanical properties. Key words low carbon bainitic steel,tempering, retained austenite, mechanical properties 高强度低碳贝氏体钢是现代物理及化学冶金技术研究成果相结合的产物，具有工艺简单、节省能源、强 韧性好、易于成型以及优良的焊接性能等优点，目前已在工程机械、造船和石油天然气输送管线等行业得到 广泛应用[1,2] 。材料的屈服强度与抗拉强度反映了钢材的力学性能指标，对材料的使用性能有重要的影响。 对于高强度钢来说，为保证其使用的安全性，要求材料既具有高的强度，低的屈强比，同时还要有较高的伸 长率要求。通过不同的热处理工艺，可以改变微合金低碳贝氏体钢中相变产物的类型、各相变组织的比例、 组织细化程度等，从而改善钢的性能。本文主要通过研究不同的回火温度对低碳贝氏体钢组织与性能的影响， 从而确定最佳的生产工艺以降低该钢板的屈强比，使钢板获得优良的综合力学性能。 1 试验材料及方法 本实验用钢由25k