CrMo钢主轴白点成因分析.pdf

一重技术 检查与测量 10.3969/j.issn.1673-3355.2011.05.014 34CrMo1 钢主轴白点成因分析 1 2 3 3 4 乙继海 , 郑承平 , 王 杰 , 刘 贺 , 张兴铎 摘要：通过低倍酸洗和扫描电镜断口分析等检测手段，对一根材质为34CrMo1 钢主轴白点的产生原因、形成机理 和预防措施等进行较为系统的分析和讨论。指出只有通过双真空或在α-Fe 的最高温度内进行保温处理，将氢含 3 量控制在不产生白点的最小极限值2 cm /100 g 以下以及减少因各类偏析所产生的组织应力，才能达到既可防止产 生白点又能提升产品质量的双重目的。 关键词：白点；组织应力；断口分析 中图分类号：TG115 文献标识码：B 文章编号：1673-3355 （2011）05-0014-04 Analysis of Flanks Exiting in 34 CrMo1 Steel Spindles Yi Jihai ，Zheng Chengping ，Wang Jie ，Liu He ，Zhang Xiaoduo Abstract: The cause and formation of flakes in a 34CrMo 1 steel spindle are studied by the means of pickling the spindle and scanning the fracture on it with low -power SEMs in the paper. Based on that, a measure is put forward to prevent the generation of flakes in steel spindles, that is to carry out the soaking treatment with double vacuum technique or below the 3 highest permissive temperature of a-Fe to control the content of hydrogen below the minimum limit value of 2 cm /100 g to avoid the generation of flakes and eliminate the structrual stress cased by various segregation, which can only only prevent flakes from generating in steel spindles but also improve the quality of products. Key words: flake ；structural stress ；fracture analysis 一根材质为34CrMo1 钢的主轴，在粗加工后 口上典型的白点缺陷清晰可见（见图3）。 探伤检测时因发现在轴身中间部位有大量密集性 超标准缺陷而报废。为确定缺陷性质，制定正确 的改进措施和提升产品质量，利用现有检测设备， 对该主轴进行了解剖分析（见图1）。 图1 取样部位示意图 1 检验方法和结果 （1）经酸洗后，发现有大量长短不等方向各 图2 横