低黏度油墨和橡皮布对无水胶印印刷导电层的影响研究.pdfVIP

78 中国印刷与包装研究 2012年第2期 (第4卷) Germany AbstractThisstudydescribestheapplicationofconductivepolymerinksontoPETfoilsbythewaterlessoffsetprintingtech— nique．Commerciallyavailableconductivepolymerink swereemployed，whichexhibitsignificnatly lowerviscositiesthna conventionaloffsetprintingink s．Th emainfocuswasputontheinfluenceoftherubberblanket，whichcoverstheblanket cylinderoftheoffsetprintingunit，onthemorphologyandelectrical propertiesoftheprintedconductivepolymerlayers． Sincefilm splittingoccursbetweensubstratenadrubberblanket，thelatteraffectstheamountofinkwhichistrnasferredby theprintingprocess．Thewetfilm thicknessoftheprintedmaterialwasdeterminedfordifferentrubberblanketspecifications nad inkingrates．Inaddition，theresistivityoftheprintedconductivepolymerlayerwasmeasuredafterflue—curingofthe samples．Further，theelectrical perfomr na ceoncorona—treatedna duntreatedPET substratefoilswascompared． KeywordsPrintedelectronics；Orgnaicelectronics；Conductivepolymers，Offsetprinting；W etting；Coronapretreatment From JournalofCoatingsTechnologyandResearch，2012，January：1—8． 低黏度油墨和橡皮布对无水胶印印刷导电层的影响研究 摘译 近年来，随着全球市场对电子器件需求量的不断增 匀性。据相关文献报道，在凹版eHSm]的过程中通常会提 长，许多科研院所及部分企业都在尝试利用传统印刷 (柔 到高黏度的油墨和橡皮布。采用该印刷工艺，以高黏度 印、凹印、网印等)和数码印刷 (喷墨印刷等)技术来制 的银墨为导电墨印制导线图案。在油墨从橡皮布转移到 作电子器件。为了实现电子器件的高沉积精度，对印刷技 承印物的过程中由橡皮布轻微变形引发的导线图案扭曲 术提出了以下几点要求：线条无缺陷，有锐边且分辨率 受到印刷压力和摩擦力的严重影响。尽管如此，依然可 高；图层无针孑L，均匀且表面光滑；墨层厚度较薄。 以实现20 m的印刷线宽。 通常，采用喷墨印刷、丝网印刷或凹版印刷技术， 为了获得均匀一致的导电层，本研究讨论和分析了 以PEDOT：PSS作为导电层用于聚合物太阳能电池等电 用于无水胶印的两种市售PEDOT：PSS油墨的印刷适 子器件的制备，到 目前，还未见使用胶印来制备PEDOT 性，以获得均匀的聚合物导电层 。重点优化了PEDOT： ：PSS导电层的报道。但胶印仍 以高分辨率、高图像质 PSS油墨的印刷适性并用电晕处理改善了承印物的润湿 量、高速和大批量低成本的显著优势成为印刷工业中最 性能。 为盛行的印刷方法，但 由于传统胶印油墨黏度较高，范 I．实验部分 围为30～100Pa·S，易于使印制的图文厚度过大，从而 ①实验条件。本实验在干净的恒温恒湿