新型离心铸造涂料性能的研究.pdfVIP

山西省第二十三次铸造会议论文集 新型离心铸造涂料性能的研究 1 1 1，* 2 2 庞铭李 ，靳玉春 ，侯 华 ，任巨良 ，毕文刚 (1.中北大学，山西 太原 030051； 2.山西高平市泫氏铸业有限公司，山西 高平 048400) 摘 要：研究了耐火粉、悬浮剂、粘结剂对水基铸造涂料悬浮性和发气量 等性能的影响以及它们之间的相互作用。实验表明：原材料对涂料的悬浮性和 发气量起着决定性的作用。 关键词：耐火粉；悬浮剂；粘结剂；发气量；悬浮性 Effect of Raw Material on Suspension Rate and Gas Evolution of Water-based Foundry Coating 1 1 1,* 2 2 PANG Mingli , JIN yuchun , Hou hua ，REN juliang ,BI Wengang （1.North university of china,Taiyuan 030051,China; 2.Shanxi Gaoping City Suns Piplines Co. Ltd,Gaoping048400,China) Abstract: The impact of the component of coating,such as refractory powder filler, adhesive and suspension-agent on the amount of gas evolution from the coating, suspension-ability of coating etc. and the interactions between the additives were investigated. The experiment results show that raw material decisive gas evolution from the coating, and suspension-ability of coating . Key words: raw material; suspension agent; adhesive ;suspension-ability; the amount of gas evolution from the coating; surface blowhole 水基铸造涂料价格低廉、安全可靠、性能稳定、运输方便、清洁无污染，在砂型铸造、 金属型铸造、离心铸造、消失模铸造等方面都有着广泛应用，是未来铸造涂料发展方向之一 [1]。在水基铸造涂料生产中，常用耐火粉有硅藻土，铝矾土等；无机悬浮剂为钠基膨润土， 锂基膨润土等；粘结剂为水玻璃，磷酸铝，硫酸铝，六聚偏磷酸钠，三聚偏磷酸钠，聚合氯 化铝等无机粘结剂。但原材料对涂料最重要的技术指标——悬浮性和发气量的影响及其相互 作用的研究，鲜有报道。本文选用硅藻土作为水基涂料的耐火粉骨料，钠基膨润土作为悬浮 剂，磷酸铝和三聚偏磷酸钠等作为粘结剂，研究了原材料对涂料的悬浮性和发气量等性能的 影响。 1 实验材料及测试方法 1.1 实验材料 硅藻土，600目(吉林长白山产)、325目(吉林长白山产)；钠基膨润土(浙江临安、美国)； 聚合氯化铝(工业用)；磷酸铝(化学纯)；三聚偏磷酸钠(工业用)；六聚偏磷酸钠(工业用)； 硅溶胶(工业用)；硫酸铝(化学纯)； 1.2 原材料及涂料性能的测试方法 悬浮性的测试方法：搅拌均匀的涂料倒入量筒内，使其达到 100ml 标高处。在密封静止 状态下，涂料试样放置 24h，再测量上部澄清层体积。悬浮率可按下式计算： — 106 —