铜及铜合金在厦门海域实海暴露腐蚀规律研究.pdfVIP

The 6th China Corrosion Conference Corrosion of Copper and Its Alloys Exposure in Xiamen Natural Seawater 1,2 2 2 1,2 Xiangfeng CHEN , Zhenjun MU , Chunsheng XU , Runtao REN 1State Key Laboratory for Marine Corrosion and Protection 2Luoyang Ship Material Research Institute, Fujian, Xiamen, 361101 Email: wind8435201@163.com Abstract: 3 kinds of typical copper and its alloys were exposed in 3 zones of seawater at Xiamen for 8 years. The regulations of corrosion of three materials in immersion zone, mean-tide zone and splash zone were summarized, and the mechanism of the corrosion was also discussed. Keywords: copper; copper alloy; seawater exposure 铜及铜合金在厦门海域实海暴露腐蚀规律研究 1,2 2 2 1,2 陈翔峰 ，穆振军 ，许春生 ，任润桃 1 海洋腐蚀与防护国防科技重点实验室 2 中船重工七二五所厦门分部，福建，厦门，361101 Email:wind8435201@163.com 摘 要：通过Tup 纯铜、B10 及B30 铜合金3 种典型的铜及铜合金在厦门海域实海暴露实验，总结了 3 种材料在厦门海域全浸区、潮差区及飞溅区的腐蚀规律，并对其腐蚀机理进行了探讨。 关键词：铜；铜合金；实海暴露 试验用材料选择典型的 TUP 纯铜和 B10 、B30 铜 1 前言 镍合金，试样尺寸为 100×200 mm，厚度 3mm 左右， 铜及铜镍合金是使用于海洋环境中的典型传统 所有试样表面用汽油、金属清洗剂除油，再用清水冲 材料，因其具有良好的耐海水腐蚀和抗海洋污损生物 洗，蒸馏水清洗，无水乙醇浸泡脱水，吹干。下样前 附着性能而得以广泛应用[1,2] 。近年来，对其在海洋环 在感量 0.01g 的天平上称量，用游标卡尺测量各块样 境下的相关性能开展的研究也十分活跃，主要针对腐 品尺寸，精确到0.02mm 。 蚀产物膜特征来探讨其耐蚀性与防污性[3] ，以及一些 本试验在厦门海域的全浸区、潮差区和飞溅区同 环境因素对铜及铜镍合金腐蚀性能的影响，如溶解氧、 时进行，试验周期为 1 年、2 年、4 年及 8 年。 氯离子浓度、湿度、污损生物的附着等[4,5