山东某钾钠长石矿提纯工艺试验研究.docVIP

山东某钾钠长石矿提纯工艺的试验研究 张凌燕潘力邱杨率黄雯 (武汉理工大学资源与环境工程学院，湖北 武汉430070) 摘要采用“磨矿一脱泥一磁选一浮选”的工艺流程，对山东某地长石矿进行精选，可以得到最终精矿中TFeO3含量O12%、CaO含量026%的技术指标，该精矿达到了我国长石产品在釉料、陶瓷白坯及平板玻璃等方面应用一级质量指标。关键词长石磨矿脱泥磁选浮选 中图分类号：TD97 文献标识码：A 文章编号2011)01-0033-04 Experimental Study on Purification Technology of Potash and Soda Feldspar Ore from Shandong Zhang Linyan Pan Li Qiu Yangshuai Huang Wen (School of Resource and Environmental Engineering，Wuhan University of Technology,Wuhan 430070) AbstractThe technological process of’grinding—desliming—magnetic separation—floatation’was adopted to concentrate the feldspar ore from Shangdong somewhere．The final concentrate could be obtained which the content of total iron oxide was 012%and calcium oxide was O.26%．This final concentrate reached the first quality standard of feldspar for glaze，white blank of porcelain and plate glass． Key words feldspar ore grinding desliming magnetic separation floatation 长石是由钾、钠、钙和钡的铝硅酸盐组成的族60%，在1100～1300℃之间，化学稳定性好，在与石英及铝硅酸。实践证实，长石中的铁、(主要以碳酸盐存)含量过高，烧成制品会出现凹凸不平的气孔，故在 长石一般与石英、云母类矿物、方解石、黏土矿物 1实验部分 1.1 矿石性质 矿样为山东某地长石矿，原矿化学(wt%)为：Si02，68.68；A120，17.37；TFe203，0.34；MgO，0.15；CaO，1.02；Na20，6.05；K20，4.64；Ti02，0.11；P205，0.04；MnO，0.02；20-，0.1l；烧1.47。原矿中Na20+K20为10.69％，低于11TFe203含量为0.34，高于02%的一级品标准，CaO含量为1.02，也高于1.0的一 原矿经XRD分析可知，矿石中主要成分为钠长49%、钾长石16、石英18和云母类矿物9，还 原矿磨矿分级后，经分析各粒级产品中铁、钙元0.030mm以下的细粒级中。 12 实验药品与仪器 实验药剂：脂肪酸盐类捕收剂，水玻璃，碳酸钠，(均为市售)。 实验仪器：XMB-70型三辊四筒磨矿机，湖北探Slon-100周期式脉动高梯度磁选机，江西RK/FD型L单槽浮选机，武汉洛XTLZφ260/φ200多用真102厂。 13 磨矿细度的确定 在磨矿浓度为50条件下，3个粒+0.074mm，0.074mm+0．045mm和0.045mm。8min、10min、12min、14min和16min，磨矿采用XMB70型三辊四筒磨矿机。试验1和图1。 由表1和图l可知，当磨矿时间从8min增加到10min时，磨矿细度变化不大；从10min增加到12min0.074mm含量增加较明显，达到了6368%，继续0.074mm和-0.045mm含量增加的趋势逐渐变小。表1磨矿细度与磨矿时间的关系表图1磨矿细度曲线 磨矿细度通过全流程试验进行确定，试验流程见2，试验结果见表2。其中混合捕收剂是一种胺类 图2磨矿细度验证试验流程图表2磨矿细度验证试验结果TFe203/% 铁去除率/% 精矿CaO/% 钙去除率/% 8 43.04 75.49 0.15 66.70 0.27 80.02 10 48.57 71.96 0.14 70.37 0.26 81.66 12 63.68 70.35 0.13 73.10 0.25 82.76 14 68.33 67.75 0.12 76.09 0.26 82.7