KOH活化法制备竹炭的研究.docVIP

KOH活化法制备竹炭的研究 作者：金祥 摘 要 以西昌市野生毛竹为原材料,用KOH作活化剂制备活性炭。采用四因素三水平的正交实验设计法分别研究了活化温度、碱炭比、活化时间、炭化时间等工艺参数对竹炭吸附性的影响，在研究中得出最佳的制备工艺是：活化温度为850 ℃，碱炭比为41，活化时间为60 min，碳化时间为2 h，制备的活性炭产品吸附性最高关键词 The research of making bamboo carbon with KOH Abstract：Activated carbon was prepared with the wild moso bamboo in Xichang city as materials and the KOH as activating agent. Some process parameters affecting the charcoal absorbability,such as activation temperature ,the ratio between alkali and carbon ,activation time,carbonization time and other factors ,have been studied by using orthogonal experimental design method of four factors and three levels.The research results showed that when activation temperature was 850℃,and the ratio between alkali and carbon was 4:1,and activation time was 60min and carbonization time was 2h,the prepared product could reach the best absorbability . Key words： Moso bamboo KOH Activation Bamboo carbon 1 前言 1.2 我国活性炭的生产发展现状1.3 活性炭的制备方法及特征 早年活性炭的制备主要是以木炭、木屑、果壳等林产品为原料的，由于林产品资源有限，近年来原料逐步转向价格低廉、储量丰富的煤炭，石油废料、废旧塑料、废旧皮革、废轮胎、造纸废料、城市垃圾等废弃物[8]。目前大都认为果壳是活性炭制备的最佳的原材料，但是我国果壳材料非常缺乏，而且不容易贮存、集中、价格昂贵。对此近年来，国内外对各种含量丰富、来源广泛、价格较低的矿物材料，废弃物等相继进行了活性炭制备试验[9]。以煤为原料制备活性炭发展非常迅速，应用范围和数量也在扩大，目前媒质活性炭使用已经超过了木质活性炭。近年来，也有一些用废旧橡胶、农林副产品、石油废料、纸浆废浆、劣质煤等许多含碳的工业原料，制造价格低廉特殊性能的活性炭。国内外利用废弃材料制备活性炭，以谋求廉价原料的探索受到了重视，如采用废塑料、废橡胶、纸浆废液、石油副产品等原料制得的活性炭，有的己投入使用，这种有效的变废为利的方法前途非常广泛[10]。 所有制备活性炭的原材料均是含碳物质，目前国内外选用的制备活性炭的主要原材料可分为以下四大类[11] (a)植物性原料:如木炭、椰子、木材、油棕壳、锯屑、树皮、竹子、稻壳、果核、果壳等 (b)矿物原料:如褐煤、泥煤、石油沥青、石油油渣等 (c)各种废弃物:如废旧皮革、废轮胎、动物的骨头和血、城市垃圾等 (d)合成纤维材料:如聚氯乙烯、酚醛树脂、聚碳酸酯、聚丙烯等 1.3.2 活性炭的制备方法 由于活性炭原料的多样性和用途不同，通常采用不同的活化方法，因此将活性炭的制备方法大致分为气体活化法、化学活化法和化学物理活化法[12]。 表一 国内部分废弃物制备活性炭的方法及其性能 原料 制备方法 活化温度(℃) 微波功率(W) 活化时间(min) 碘吸附值(mg/g) 收率(%) 竹节及其炭化料 微波辐射氯化锌（40%）法 微波辐射水蒸气法 —— —— 359 700 5 7 1088.4 1012.2 39.2 52.3 毛竹 微波辐射氯化锌（50%）法 —— 720 22 1062.3 —— 烟杆废料 微波辐射氯化锌（50%）法 微波辐射水蒸气法 高温经氯化锌溶液浸渍12h —— —— 800 750 700 —— 7 6 120 1093.4 1018.7 1018.3 34.7 20.7 —— 甘蔗渣 微波磷酸法（15%～25%） —— 720