表面活性剂对纳米氧化锌准备的影响.DOCVIP

表面活性剂对纳米氧化锌制备的影响 作者：金祥 摘 要：纳米氧化锌的制取方法很多，但都有不足的地方。本篇论文选择微乳液的方法制备纳米氧化锌。微乳液法具有操作简单、粒径可控、生成粒子的尺寸比较均匀等优点。采用微乳液法制备的纳米氧化锌,用六水合硝酸锌为原材料、OP-10为主表面活性剂、正丁醇为助表面活性剂经过实验处理得到纳米氧化锌。论文中探讨了影响纳米氧化锌生成的因素，结果表明，最佳工艺条件为主表面活性剂与助表明活性剂之比是31、硝酸锌溶液的浓度为1.0 mol/L。并用XRD、激光颗粒分布仪表征。Preparation Of Nano Zinc Oxide Abstract: Preparation of ZnO Nanoparticles have many ways,But many are inadequate. This thesis Select microemulsion prepared nano-zinc oxide.Microemulsion methods are simple,controllable particle size, more uniform particle size.Generated.Zinc Oxide prepared using microemulsion method,with zinc nitrate hexahydrate as raw material,OP-10 as surfactant,n-octanol as cosurfactant ,through experimental treatment get Zinc Oxide.Paper explored the factors that influence the resulting nano-zinc oxide,The results show the optimum conditions with the ratio of surfactant and cosurfactant is 3:1.The concentration of zinc nitrate solution was 1.0mol/L.And use XRD and laser particle size distribution to detect. Key Words: surface active agent nanometer zinc oxide preparation 1 前言 1.1 氧化锌简介 氧化锌是一种常用的化学添加剂，广泛地应用于塑料、硅酸盐制品、合成橡胶、润滑油、油漆涂料、药膏、粘合剂、食品、电池、阻燃剂等产品的制作中。氧化锌的能带隙和激子束缚能较大，透明度高，有优异的常温发光性能，在半导体领域的液晶显示器、薄膜晶体管、发光二极管等产品中均有应用。此外，纳米氧化锌作为新型的无机功能材料，具有表面与界面效应、量子尺寸效应、体积效应和高透明度、高分散性等特点，在电压材料、光电材料、图像记录材料、橡胶、涂料、化妆品等行业具有广泛的应用，因而制备技术和工业生产的研究也变得更为重要。 1.2 纳米氧化锌的制备进展 1.2.1 直接沉淀法制备纳米氧化锌 在可溶性锌盐溶液（二水合醋酸锌，化学纯）中加入沉淀剂，在一定条件下反应生成沉淀，再经过分离和洗涤沉淀物，除去其中的杂质离子，最后干燥、热分解，得到纳米氧化锌。 反应过程：Zn(CH2COO)2+NH4HCO3 → Zn5(OH)6(CO3)2+CH3COONH4+CO2+H2O Zn5(OH)6(CO)2 → ZnO+CO2+H2O 1.2.2 均匀沉淀法制备纳米氧化锌 均匀沉淀法是利用某一化学反应使溶液中的构晶离子由溶液中缓慢地、均匀地释放 出来。此时，加入的沉淀剂不是立刻与被沉淀组分发生反应，而是通过化学反应使沉淀剂在整个溶液中缓慢地生成。其优点之一是构晶离子的过饱和度在整个溶液中比较均匀，所以沉淀物的颗粒均匀而致密，便于过滤洗涤。同时，它可以避免杂质的共沉淀，这样得到的粒子粒径分布均匀。 1.2.3 溶胶-凝胶法制备纳米氧化锌 溶胶-凝胶法是化学和材料领域中重要的制备方法，通常以金属醇盐及酸盐为原料，在有机介质中进行水解、缩聚，使溶液经溶胶-凝胶化过程得到凝胶，进而干燥、煅烧。该法的优点是产物粒度均匀、纯度高、反应易控制，但成本较高。 1.2.4 微乳液法制备纳米氧化锌 微乳液通常是由表面活性剂、助表面活性剂、油和水在适当的比例下自发形成的外观为透明或半透明、各向同性、热力学稳定的分散体系，其分散相单体微液滴直径一般在10~50 nm范围，界面层厚度通常为2~5 nm，由于分散相尺寸远小