烟囱用钛%2f钢复合板应用与其耐蚀性能探讨.pdfVIP

(2)有色金属材料 烟囱用钛/钢复合板应用及其耐蚀性能探讨 王虎年 朱磊 李平仓 华先锋 张文平 吕刚 （西安天力金属复合材料有限公司，陕西西安 710201 ） （陕西省层状金属复合材料工程研究中心陕西 西安 710201 ） 摘 要：目前国内外烟囱内衬钛复合板需求量极大而且应用广泛，但对其耐蚀情况开展的研究相对较 少，本文对烟气环境进行了简要介绍，并对该领域的耐蚀研究现状进行了调研，并指出后续耐蚀研究 应该重点结合烟气流速、烟道承受压力和酸液浓度等关键参数来开展。 关键词：烟囱;钛－钢复合板;耐蚀性能 The applic ation and corrosion resistance discus sion of titanium clad plate in chimney WANG Hunian, ZHU Lei, LI Pingcang, HUA Xianfeng, ZHANG Wenping, LV Gang (Xi ’an TianLi Clad Metal Materials Co., Ltd; Shaanxi Layer Metal Clad Material Engineering Research Center, Xi -an 710201) Abstract：There are very limited researches on corrosion resistance of titanium clad plate in chimney lining， though its ’ very heavy demands and wide applications. Flue environment is introduced briefly in this paper, The research actualities of corrosion resistance also have been studied, corrosion resistance combine key parameters, such as velocity of flue, the pressure of flue pipe and acid concentration should be studied in following research. Key words ：chimney ; titanium clad plate; corrosion resistance 一、烟气环境简介 随着国家环保标准的逐步提高和国民环境意识的增强，国内新建燃煤发电机组都要求对 排放烟气进行脱硫处理，对于烟囱的防腐设计，各电力设计院都进行了长期的摸索和探求， 以期达到安全可靠、耐久经济，对于钢内筒结构，在烟气湿法脱硫（无GGH装置）的情况下， 国际工业烟囱协会（CICIND）在其发布的《钢烟囱标准规程 》 （1999年第一版）中建议采用普通碳钢板在其内侧（接触烟气）增加一层非常薄的合金板 或钛板的方法进行处理。目前国内电力设计院采用较为成熟的是石灰石湿法脱硫工艺（FGD）， 并在FGD系统中不设烟气加热器（GGH）装置，选用的钛钢复合板烟囱内衬钛层材质为绝大 部分为TA2，钛复层厚度为1.0～1.6mm。据资料报道，烟气经过脱硫后，虽然烟气中90%左 右的SO2被除去，但是对造成烟气腐蚀主要成分的SO3脱除效率不高，只有20%左右，因此 烟气湿法脱硫后对烟囱的腐蚀隐患并未消除。该类系统烟气温度一般在40~50℃，烟囱内壁 有严重的结露，沿筒壁有结露的酸液流淌。以一台600MW机组来说，烟气中水气结露后形成 的具有腐蚀性水液理论计算量约40~50吨/小时，它主要依附于烟囱内侧壁流至专设的排液 口排到脱硫系统的废液池中。该类烟气还具有以下特点： 1、烟气中水份含量高，烟气湿度大； 2、烟气温度低，脱硫后的烟气温度一般在40～50摄氏度 3、烟气中含有酸性氧化物，使烟气的酸露点温度降低； 作者简介：王虎年，工程师，whn@ (2)有色金属材料