转炉炼钢利用废钢地研究综述.pdfVIP

转炉炼钢利用废钢的研究综述 1 2 1 2 1 杨文远 张先贵 杨 勇 刘路长 高卫涛 （1. 钢铁研究总院, 北京 100081 ；2. 武汉钢铁公司，武汉 430080 ）1 摘 要 2010 年我国转炉炼钢废钢比平均为7.6%，欧美国家转炉为20%左右。国外冶金工作者在实验室和钢厂进 行了大量转炉利用废钢技术的研究，例如转炉合理的废钢加入量、废钢熔化速度、测定熔池温度和碳的传输系数、 冶炼优质钢时合理地利用废钢等问题。我国对于转炉利用废钢的生产技术和基础理论研究工作都应加强。 关键词 转炉炼钢 废钢比 传热 传质 The Study Overview of Utilizing Scrap in Convertor Steelmaking Yang Wenyuan1 Zhang Xiangui2 Yang Yong1 Liu Luchang2 Gao Weitao1 (1. Central Iron and Steel Research Institute, Beijing, 100081； 2. Wuhan Iron and Steel (Group) Corporation，Wuhan, 430080) Abstract In 2010, the average scrap ratio of convertor steelmaking was 7.6% in our country, and that was about 20% in the US and Europe. Foreign Metallurgical workers have done considerable technological research works about the use of scrap in convertor in the laboratories and steel mills. Such as the reasonable scrap addition in convertor, melting rate of scrap, measuring the molten bath temperature and carbon transfer coefficient, and utilizing scrap during smelting the high-quality steel etc. We should strengthen study technology and fundamental research works about the use of scrap in convertor. Key words convertor steelmaking, scrap ratio, heat transfer, mass transfer 1 我国转炉利用废钢的状况 2010 年我国转炉钢产量约为5.49 亿吨，转炉炼钢的废钢用量平均为7.6% 。欧美国家一般为20%左右。 西欧和北美的废钢来源充足，价格低于铁水，废钢的加工、配送系统也很齐全。 我国社会废钢产量不多，根据中国废钢应用协会统计资料，2009 年我国废钢平均单耗为146kg/t 钢[1]， 全世界平均水平为400~450kg/t 钢。我国转炉炼钢废钢平均消耗比欧美国家低 135kg/t 钢，2010 年全年多消 耗铁水7938 万吨。原材料消耗、废弃物产量的增加数量见表1。 表 1 转炉低废钢比所造成的物料增加量 物料名称 铁水/万吨 标准煤/万吨 精矿粉/亿吨 CO 排放/亿m3