连铸中间包涂料过度烧结的分析.pdfVIP

1连铸中间包涂料过度烧结分析 李雪冬 王米娜 范青松 傅秋华 （濮阳濮耐高温材料(集团)股份有限公司，濮阳 457100 ） 摘 要 本文采用X射线衍射分析、扫描电子显微镜和微区能谱分析等手段，通过研究一种中间包涂料在使用后的 显微形貌和物相组成，探讨了该涂料在使用过程中过度烧结的原因。认为中间包涂料在使用后生成了大量钙镁橄榄 石等低熔点物质是导致涂料烧结严重的主要因素。根据分析结论提出了控制涂料过度烧结的改进建议。 关键词 中间包 涂料 显微结构 烧结 Research on Over-sintering of the Continuous Casting Tundish Coating Li Xuedong Wang Mina Fan Qingsong Fu Qiuhua (Beijing RD Center of Puyang Refractories Group Co.,Ltd, ) Abstract The reasons for over-sintering of tundish coating during used were discussed in this paper. The microstructure and phase composition of used coating were researched by means of X-ray diffraction, scanning electron microscopy and energy dispersive spectroscopy microanalysis. A large number of low melting point materials such as monticelite were formed in tundish coating after use, which was the main factor of over-sintering. Some improvement suggestions for controlling over-sintering of coating were given according to the conclusions. Key words tundish ，coating，microstructure ，sintering 随着连铸工艺的优化及对高品质连铸坯质量要求的提高，中间包已经成钢铁生产过程中的关键环节之 一。1995 年以前，中间包工作衬主要以硅质绝热板为主，使用寿命偏低，抗侵蚀性差；而且对钢水有污染。 1995 年以后，中间包工作衬材料逐步被镁质或镁钙质涂料所取代。采用镁质材料除了使用寿命大幅度提高 外，还可以对钢水起到净化作用[1] 。 根据连铸中间包的使用条件，对涂料的要求主要有以下几点：施工简单、方便；同永久衬粘附性好、不 回落坍塌；施工完后工作衬无裂纹、烘烤时不爆裂、不剥落；使用过程中抗钢水和熔渣侵蚀、渗透能力强； 对于用后解体性能优异、翻包清渣壳容易；具有良好的保温性能。中间包涂料在使用过程中如果过度烧结， 不仅会造成中间包导热系数变大，增加钢水的温降，而且由于工作衬和中间包永久衬之间烧结还会造成中间 包翻包困难、永久衬的寿命降低，增加耐火材料综合消耗。 为了研究中间包涂料过度烧结的原因，我们对一种使用后烧结严重的中间包涂料进行了分析。通过对比 使用前、后涂料的体积密度变化和结合扫描电子显微镜(FESEM)显微结构分析以及微区(EDS)分析，对涂料 在使用后过度烧结的因素进行了探讨。 1 实验结果 1.1 涂料的性能和宏观结构变化 目前所使用中间包涂料的主要原料为镁砂，为了增加涂料的涂抹性能和烘烤时的中温强度，还需要加入 李雪冬，男，工程师，从事耐火材料研究，lixuedong@ 8-26 第八届（2011 ）中国钢铁年会论文集 一些如硅微粉、粘土粉、三聚磷酸钠等添加剂[2,3] 。