芯棒表面缺陷分析及其提高芯棒使用寿命探讨.pdfVIP

芯棒表面缺陷分析及提高芯棒使用寿命探讨 罗永强 （鞍钢生产协力中心，鞍山 114021 ） 摘 要 连轧管机组限动芯棒工作环境极为恶劣，需要经受激冷激热的热循环应力和循环交变机械应力的同时作 用，因此对芯棒材料的韧性耐热疲劳性和表面质量要求非常高。因为它不仅对轧制管材的质量有重要的影响，而且， 作为高值易耗品，芯棒的使用寿命对管材生产成本也起决定性的作用。 关键词 芯棒 表面缺陷 热疲劳 Mandrel Surface Deficiency Analysis and Raise Mandrel Service Life Study Luo Yongqiang （Production Cooperate center of Anshan Iron and Steel Group Corporation, Anshan ,114021 ） Abstract The working condition that retained mandrel of tandem rolling tube machine is extremely bad. Need to do the operation by heat cycle stress and cycle alternation mechanical stress of quench and heat shock at the same time. It is very high request of tenacity 、heat fatigue durability and surface quality of mandrel material. Because of that will not only effect rolling tube quality but also have decisive function for mandrel service life as high-value consumption goods. Key words mandrel, surface deficiency, heat fatigue 连轧管机用限动芯棒是无缝钢管连轧机组的重要热变形工具，由于芯棒工作环境极为恶劣，需要 经受激冷激热的热循环应力和循环交变机械应力的同时作用，对芯棒材料的韧性耐热疲劳性和表面质 量要求非常高，芯棒发生局部裂纹和磨损过快是当前钢管轧制生产中存在的主要问题。鞍钢无缝厂 159MPM 机组在生产投产以来钢管生产中，发现使用的芯棒出现微裂、龟裂和环裂等缺陷，致使其寿 命严重降低，且由于缺陷较深，无法改车，难以再利用，不仅使轧制钢管的内表面质量受到影响，而 且也造成生产成本大幅增加。因此，改进芯棒的性能，提高其使用寿命已刻不容缓。影响芯棒寿命的 因素有很多，如钢的材质、热加工工艺、冷加工工艺、热处理工艺、使用环境(温度、应力、热循环等) 、 结构及工艺系统、芯棒的保管维护等，本文主要从生产使用环节对芯棒表面产生缺陷原因进行研究， 通过试验和分析，确定影响芯棒使用寿命的主要因素，并有针对性的进行采取措施，这样对降低生产 成本具有重要意义。 1 芯棒用材及其特性 作为内用热工具的轧管芯棒因其工作条件苛刻，应该选用高级的热模具钢制作。鞍钢无缝钢管厂 159MPM 机组使用的热轧芯棒材质为 X40CrMoV5-1 ，此材料是一种空冷硬化的热作模具钢，其成分见 表 1。 芯棒表面缺陷分析及提高芯棒使用寿命探讨 8-321 表1 X40CrMoV5-1 钢成分（％） 元素 C Cr Mo V Si Mn S P+S 含量 0.37～0.42 4.5～5.5 1.0～1.5 0.8～1.2 0.7～1.2 0．03 ≤0 ．008 ≤0.02 X40CrMoV5-1 钢具有优异的塑韧性、高的热稳定性和耐磨性、较高的高温强度和良好