Material Sciences 材料科学, 2011, 1, 37-41 doi:10.4236/ms.2011.12007 Published Online July 2011 (/journal/ms/) Cu Addition Effect on Soft Magnetic Properties in Fe-B-C-Cu Alloy System 1,2 1 2 2 1* Xingdu Fan , He Men , Jinghua Jiang , Aibin Ma , Baolong Shen 1Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Key Laboratory of Magnetic Materials and De- vices, Ningbo Institute of Materials Technology Engineering, Chinese Academy of Sciences, Ningbo 2College of Mechanics and Materials, Hohai University, Nanjing Email: blshen@ Received: Apr. 25th, 2011; revised: May 12th, 2011; accepted: May 17th, 2011. Abstract: In this study, the microstructures and soft magnetic properties of Fe-B-C-Cu alloys prepared by annealing the melt-spun ribbons have been investigated by DSC, XRD, TEM, VSM, AC and DC B-H tracer measurement. The results show that in Fe B C Cu alloy system, the addition of Cu element takes great 84–x 10 6 x effect on the precipitation of α-Fe, coercivity (Hc) decreases with increasing x and exhibits a minimum at x = 1.0, then H increases. And magnetic flux density (B ) shows an increasing tendency due to the precipitation c s of α-Fe. When x = 1.0, the alloy exhibits excellent magnetic properties with a high B of 1.78 T, low H of 5.1 s c A/m and low core loss of 0.34 W/kg at 1.0 T and 50 Hz. Keywords: Soft Magnetic Alloy; Fe-Based Nanocrystalline Alloy; Soft Magnetic Property