煤层压裂专用轻质陶粒支撑剂的研究.doc

粉煤灰基煤层压裂支撑剂的研究 高如琴1，吴洁琰1，王紫括2,郝丹迪1， (1 华北水利水电学院,河南 郑州，450011; 2 河南大学, 河南 开封，475001) 摘要: 采用粉煤灰为主要原料(，铝矾土、高岭土、长石为助剂,制备轻质粉煤灰基支撑剂。结合TG-DTA、SEM、EDS、XRD等现代测试手段对样品的结构和性能进行了表征。结果表明：材料主要以O、Al、Si等元素为主，主晶相为莫来石和石英等，晶粒之间有大量5~10μm的气孔粒径为0.5~mm的煤层压裂陶粒支撑剂，体密度为g/cm3，视密度为g/cm3，0.284%，22Mpa条件下，抗压破碎率为%，导流能力67.24 μm2·㎝。 结构和性能TQ174 文献标示码：Apropping agent of fly-ash based for coal seam fracturing GAO Ru-qin1, WU Jie-yan1, WANG Zikuo2, HAO Dan-di1 （1. North China University of Water Resources and Electric Power，Zhengzhou 450011adding bauxite, kaolin and feldspar and calcium as aids, lightweight fly ash ceramsite propping agent was produced. By the means of TG-DTA, XRD, SEM and other modern means of testing, the structure and properties of the samples were characterized. The results show the materials has preferable sphericity, and mainly consist of O、Al、Si and other elements. Its main phase is mullite and quartz, and the grain size of a large number of 5 ~ 10 microns between stomata. The?volume density, apparent density and acid solubility of proppant in coal seams fracturing that has a particle size of 0.5 ~0.8 mm are 0.998g/cm3，the 2.559g/cm3 and 0.284% and 9.241% respectively. In 22MPa, the broken rate and flow conductivity are 9.241% and 67.24μm2·㎝racturing of coal seam; proppant; structure and properties 我国煤层气资源非常丰富，它主要以吸附状态存在于煤层的内表面上，埋深在2000米以上的产量约为3.45×1013m3,位于世界第三[1]，与常规天然气储量相当。煤层气又称为“瓦斯”，主要成分为甲烷，是一种清洁高效的能源，具有埋藏浅、温度低、抗压强度低、渗透性差等特点[2,3]。要实现煤层气的工业化开采和利用，必须人为地对其施加增产措施。目前国内外最常用的增产措施是水力压裂技术[4,5]，支撑剂是煤层气井压裂增产的关键材料，对支撑裂缝、防止裂缝重新闭合、煤层气的开采率及产量的提高有着重大影响[6]。目前国内外常用支撑剂是石英砂和石油开采用陶粒支撑剂，而石英砂具有圆球度差表面光洁度低抗压强度低受嵌入、粒运移、堵塞等因素的影响，导流能力降低可降低或更低。 1.1原料 粉煤灰选自郑州市新力热电厂，其主要化学成分为：SiO2 41.53 %，Al2O3 37.38 %, 另含有少量的Fe2O3、CaO、K2O等12.98 um；铝矾土，400目余1.8 %，产地为河南巩义，Al2O3含量为73 %(质量分数)，工业纯；烧结助剂（高岭土，长石）；助磨剂为油酸。 1.2样品制备与表征 将粉煤灰、铝矾土、高岭土、长石6～10mm1: 3）的实验室KM-I高效快速研磨机内研磨0min出磨不断加料喷水，粒径在0.5mm 的球体（30min），经干燥1180℃煅烧2h），制备粉煤灰基陶粒支撑剂。 以A12O3粉末为参比物，在空气气氛中，以20 ℃/min升温速度，用德国NETZSCH STA 499C综合热分析仪对复合材料进行热分析（T