锰氧化物合成及催化酯化反应的研究（本科）毕业设计论文.docVIP

锰氧化物合成及催化酯化反应的研究 摘 要：本论文通过对一系列纳米结构锰氧化物的制备及对其性质的表征，旨在寻找具有特殊性能的新型催化剂及其制备方法。实验利用Zn(Ac)2 和Mn(Ac)2为原料，H2O2为氧化剂在NaOH溶液中共沉淀制备ZnMn2O4。基于这种方法，改变反应条件（反应物摩尔配比，氧化剂用量，陈化时间，反应温度等）最终在常温常压的温和条件下得到了单一晶形的均匀纳米颗粒，粒径在10nm ~20nm。α-MnO2纳米线，λ-MnO2纳米颗粒。最后利用XRD，TEM对所制得的产品进行表征。 利用在不同条件下制得的一系列锰的氧化物催化合成乙酸异戊酯，分别得到其酯化率为：α-MnO2纳米线：80%左右；λ-MnO2纳米颗粒：86%左右；ZnMn2O4（煅烧200℃~500℃）：88%~94%。 关键词：纳米结构锰氧化物；纳米颗粒；水热法；乙酸异戊酯；酯化率 Abstract: In order to look for the method of preparing new pattern of catalyst，which had some special performances, we prepared a chain of nanostructured manganese oxides and attributed their behavior in this articles. ZnAc)2 and Mn(Ac)2 were used to prepare ZnMn2O4 in the NaOH solution by the oxidizer of H2O2. Based on such a method, we transferred reaction conditions, such as the mol matching of the reactant, oxidizer dosage, ageing time , reaction temperature and so on. Ultimately, we had received unique crystal form and uniform nanoparticles, their diameter is about 10nm ~20nm. Meanwhile, α-MnO2 nanolines and λ- MnO2 nanoparticles were synthesized by the method of hydrothermal synthesis. Finally，XRD and TEM techniques were used to characterize the as-prepared products. Then we synthesized isoamyl acetate by using manganic oxide that been synthesized in different condition. The esterification ratio was concluded that α-MnO2 nanolines: about 80%, λ- MnO2 nanoparticles: about 86%, ZnMn2O4 (furnacing200℃~ 500℃)：88%~94%. nanoparticles; hydrothermal synthesis; isoamyl acetate; esterification ratio 毕业设计（论文）原创性声明和使用授权说明 原创性声明 本人郑重承诺：所呈交的毕业设计（论文），是我个人在指导教师的指导下进行的研究工作及取得的成果。尽我所知，除文中特别加以标注和致谢的地方外，不包含其他人或组织已经发表或公布过的研究成果，也不包含我为获得 及其它教育机构的学位或学历而使用过的材料。对本研究提供过帮助和做出过贡献的个人或集体，均已在文中作了明确的说明并表示了谢意。 作 者 签 名：　　 　 　　日　 期：　　 　 　　 指导教师签名：　　 　 　　 日　　期：　　 　 　　 使用授权说明 本人完全了解 大学关于收集、保存、使用毕业设计（论文）的规定，即：按照学校要求提交毕业设计（论文）的印刷本和电子版本；学校有权保存毕业设计（论文）的印刷本和电子版，并提供目录检索与阅览服务；学校可以采用影印、缩印、数字化或其它复制手段保存论文；在不以赢利为目的前提下，学校可以公布论文的部分或全部内容。 作者签名：　　 　 　　 日　 期：　　 　 　　 学位论文原创性声明 本人郑重声明：所呈交