结扎橡皮圈应力松弛的研究.docVIP

结扎橡皮圈应力松弛的研究 【摘要】 目的 通过定期测量结扎橡皮圈负载后应力的变化，研究它应力松弛的过程及在不同负载下应力松弛率的异同。方法 选取结扎橡皮圈30个，随机分为3组，每组10个，3组试样分别负载100g、150g和200g。通过定期测量结扎橡皮圈在不同负载下的应力，了解应力的变化过程。对3组试样的应力变化进行统计分析。结果 结扎橡皮圈在最初的48h内应力衰减较快，负载48h后残余应力为初始应力的80%左右（78.4%～83.5%），之后应力松弛的速率逐渐减小，至第32天时残余应力为初始应力的73.1%～85.8%。结论 结扎橡皮圈在不同负载下均存在应力松弛的现象，应力松弛率相同。 　　【关键词】 结扎橡皮圈；应力；应力松弛 　　【Abstract】 Objective By way of measure the stress of elastomeric ligatures periodically after three different loads were load on, to evaluate the stress relaxation of it. And compare the stress relaxation of the three different loads. Methods The randomly selection elastomeric ligatures thirty, divide into three groups randomly, each group of ten, every group distinction load 100 grams, 150 grams and 200 grams. In this experiment measure the stress of elastomeric ligatures under different load regularly. Carries on the comparison to different load rate of changes and makes the statistical analysis. Results This research discovered elastomeric ligatures are biggest in the experimental initial 48 hour internal stress weaken, after load 48 hours remaining stress for about initial stress 80%(78.4%～83.5%). After 48 hours their stress relaxation speed reduces gradually, to 32nd day remaining stress for initial stress 73.1%～85.8%. Conclusion The rate of stress relaxation of the rubber ring ligatures on different loads are the same. 　　【Key words】 rubber ring ligatures；stress；stress relaxation 　　应力松弛［1］是指在恒定温度下，快速施加外力，使试样产生一定的形变（或应变），维持这一形变所需的应力（等于试样内部的内应力）随时间增长而逐渐衰减的现象。线形高分子聚合物应力松弛的分子机理［2］为试样被拉伸时张力迅速作用使缠绕的分子链伸长，但这种伸长的构象是不平衡的，由于热运动分子链会重新卷曲，但形变量被固定不变，于是分子链可能解缠结，出现应力松弛。 　　利用结扎橡皮圈进行主动结扎关闭间隙的方法是由McLaughlin、Bennett和Trivisi 3人提出的［3］，并随着MBT直丝弓矫治技术的快速推广而广泛应用,为了解结扎橡皮圈在正畸治疗中所产生矫治力的变化情况，就必须研究它应力松弛的过程，同时此项研究也将为口腔正畸医师在临床工作中决定初始矫治力的大小以及复诊间隔提供依据。 　　1 对象与方法 　　1.1 研究对象 选用口腔正畸临床工作中最常用且较具有代表性的结扎橡皮圈 Classone Orthodontics solo tie(clear)作为研究对象。本研究随机选取单个结扎橡皮圈30个作为研究对象。 　　1.2 研究方法 将单个结扎橡皮圈随机分为3组，每组10个。第一组负载100g，第二组负载150