新型耐高温低压反渗透复合膜的分离性能+.pdf

C059 新型耐高温低压反渗透复合膜的分离性能 武春瑞 张守海 颜春 蹇锡高? （大连理工大学高分子材料系 辽宁 大连 116012 ） 摘 要 以含二氮杂萘酮结构的聚芳醚砜酮超滤膜为支撑层，通过界面聚合法制备聚酰胺复合 膜。考察了操作条件对复合膜性能的影响。随着压力和温度的升高，膜的通量迅速增加而对NaCl 的截留率基本不变。在 1.6MPa、80℃下对 1000ppmNaCl截留率超过 99% ，渗透通量约为 55 -2 -1 L·m ·h 。该膜在高温下对多种无机盐及低分子有机物都表现出较高的截留率。 关键词 聚芳醚砜酮（PPESK ） 界面聚合 复合膜 耐高温 SEPARATION PROPERTIES OF NOVEL THERMAL STABLE LOW PRESSURE REVERSE OSMOSIS COMPOSITE MEMBRNE WU Chunrui , ZHANG Shouhai , YAN Chun and JIAN Xigao (Department of Polymer Materials, Dalian University of Technology , Dalian 116012,Liaoning China) Abstract Thermostable composite membrane was prepared through interfacial polymerization of m-phenyl diamine and trimesoyl chloride on poly(phthalazinone ether sulfone ketone) (PPESK) ultrafiltration membrane. The effects of the operating conditions on the performance of the membrane were studied. The flux of the membrane increased dramatically with the increase of operating temperature and pressure but no significant change was observed on the rejection of the membrane. The rejection of the membrane to 1000ppm NaCl solution was over 99% and the -2 -1 permeation flux was about 55 L·m ·h when tested under 1.6MPa at 80 ℃. The membrane shows high rejection to many inorganic salts and some organisms with low molecular weight. Key words poly(phthalazinone ether sulfone ketone)(PPESK), interfacial polymerization, composite membrane, thermal stable 联系人：蹇锡高。 第一作者：武春瑞，男，25 岁，博士研究生。 基金项目：国家 863 计划项目（项目编号：2003AA33g030 ）、国家“973 ”基础研究计划项目（项目编 号：2003CB615700 ）的部分内容。 引 言 膜分离技术从上世纪 60 年代开始得到了迅速发展，已经广泛应用于水的脱盐和纯化、 石油化工、轻工、纺织、食品、生物技术、医药、环境保护等领域[1]。反渗透膜分离技术是 目前最便捷、高效的海水和苦咸水淡化的方式，同时也是处理含有低分子有机物的工业废水 的重要手段之一[2]。目前生产的反渗透膜大多只能在低于 45℃的条件