04-水清洗对空气净化材料过滤性能影响-刘晓培.doc

水清洗对空气净化材料过滤性能的影响 刘晓培，卞思思，常德强，毛宁，柳静献，孙熙 （东北大学滤料检测中心，沈阳，110004） 摘要：用于空气净化的材料一般为一次性使用，但有的应用场所需要对其进行反复水清洗多次使用。本文通过实验手段，研究常规涤纶纤维层滤料，在荷尘、清洗、烘干、荷尘等多次反复中其过滤效率、阻力、容尘量的变化情况。实验结果表明，清洗对滤料的过滤效率、阻力和容尘量没有明显的影响，滤料可以通过水清洗的方式反复使用。 关键词：空气净化材料；水清洗；过滤性能 Effect of water cleaning on performance of air filtration medias LIU Xiaopei, BIAN Sisi, CHANG Deqiang, MAO Ning, LIU Jingxian, SUN Xi (Filter Test Center of Northeastern University, Shenyang,110004) Abstract: Air filtration media are designed for disposable, but in some application, it should be used for some times with water cleaning. Through experiments, the performances of filter, which are cleaned with water for many times, including filtration efficiency, resistance, dust capacity are studied in the paper. The experimental results show that water cleaning has less effect on filtration efficiency, resistance and dust capacity of the filter media. Therefore, air filtration media can be used repeatedly by way of water cleaning. Keywords: Air filtration media; water cleaning; filtration performance 1 前言 随着我国社会发展及工业进程的加快，不管民用还是工业对环境空气质量的要求越来越高，空气过滤设备的应用领域也在加速拓展，而作为过滤设备的核心——空气净化材料，其研究和开发得到了人们的广泛关注。人们期望过滤材料具有高效率、低阻力的特性，并能适用于多种环境，且成本越低越好。[1-3] 用于空气净化的大部分材料为一次性使用，在应用时如果其阻力达到一定值后，该过滤器即被抛弃。[4]此方式在保证空气过滤效果的同时，提高了空气净化的成本，增加了过滤器更换的工作量。另外，在某些特殊场合，如机车、船舶等移动式设备，频繁更换十分方便，迫切要求可清洗型过滤产品。[5-6] 基于上述考虑，本文以用量最大的常规涤纶纤维层滤料为例，研究其在荷尘、清洗、烘干，再反复荷尘、清洗多次使用中，其过滤效率、阻力、容尘量的变化情况，以确定滤料在反复使用中性能的变化，为滤料的重复使用提供实验参考。[7-9] 2 实验方法及装置 2.1 实验条件及装置 本文选取了丹东某厂家生产的4种常规的涤纶纤维层净化材料，进行了实验研究，滤料样品的性能参数如表1所示，电镜照片如图1-图4所示。 表1 样品的性能参数 项目 样品A 样品B 样品C 样品D 类别 强化中效过滤材料 中效过滤材料F7 中效过滤材料F5 低效过滤材料G4 克重(g/m2) 354.88 259.61 266.54 316.68 厚度（mm） 11.8 7.2 8.9 10.0 滤速为1.2m/s时的阻力(Pa) 218 147 115 56 纤维层主纤维 不同直径的中空与常规涤纶纤维 不同直径的中空与常规涤纶纤维 不同直径的中空与常规涤纶纤维 不同直径的中空与常规涤纶纤维 粘结纤维 ES ES ES ES 加工方式 ES纤维热熔粘结 ES纤维热熔粘结 ES纤维热熔粘结 ES纤维热熔粘结 后处理 阻燃处理 阻燃处理 阻燃处理 阻燃处理 图1 强化中效过滤材料的迎尘面和底层 图2 中效过滤材料F7的迎尘面和底层 图3 中效过滤材料F5的迎尘面和底层 图4 初效过滤材料的迎尘面和底层 实验中采用的装置如图5所示。该装置由管道系统、发尘系统、测压系统组成。尘源为325目的滑石粉，发尘浓度为3.385