Hot Working Technology 2013 ,Vo 1. 42 ,No.14 AZ31 上高能微弧火花合金化AI-Ce 的 质量转移特征 邱璋1，陈长军 2，张敏2 (1.长沙理工大学能动学院，湖南长沙 410114; 2. 苏州大学激光加工中心机电工程学院，江苏苏州 215021) 摘 要:采用 AI-Ce 合金作电极在不同参数下对AZ3l 续合金进行合金化，以确定基材的质量增加、电极的质量增 加和相应的质量转移系数。结果发现在电极和基材表面均存在飞溅特征。 关键词:高能微弧火花合金化(电火花合金化);续合金;铝-销合金;质量转移 中图分类号:TG159 文献标i只码:A 文章编号: 1001-3814(2013)14-0122-04 Mass Transfer Characteristics of High-energy Micro-arc Alloying AI-Ce on AZ31 Alloy 2 2 QIU Weï1, CHEN Changjun , ZHANG Min (1. School of Energy and Power Engineering, Changsha University of Science and Technology, Changsha 410114 , China; 2. School of Mechanical and Electrical Engineering, Laser Processing Research Center, Suzhow University, Suzhou 215021 , China) Abs仕act: The AI-Ce electrode was applied to AZ31 magnesiurn alloy in several process p缸ametersωdetermine the effect ofparameters on the cathode gain (CMG), anode mass gain (AMG) and mass transfer coefficient 仙ITC). The results show that splash spots occur on both the electrode and the substrate surfaces. Mass transferred 企Om electrode to substrate each o也.er occurs simultaneously. Key words: high-energy micro-arc alloying (elec创c sp缸k alloying); Mg alloy; AI-Ce alloy; mass 位ansfer 是通过多次放电、反复合金化形成的强化点逐渐叠 镜及其合金由于质量轻、比强度和比刚度高而 加产生的问。一次放电的质量转移的量很微小，通过 在航空航天、汽车、电子通讯等行业的应用得到迅猛 直接测量的方法获得质量转移的特性参数变得非常困 发展。然而，镜及其合金的耐蚀性差限制了其在这 难。因此关于合金化层的质量转移规律，目前主要有 些领域的应用。在楼合金上制备防护性涂层的技术 三种假设:第一种假设[句认为在电脉冲