Anodic Behavior of Zn-Al-Be Alloys in NaCl Solution and the Influence of Be on Structure英文文献资料.docVIP

Journal of Surface Engineered Materials and Advanced Technology, 2012, 2, 127-131 127 /10.4236/jsemat.2012.22020 Published Online April 2012 (http://www.SciRP.org/journal/jsemat) Anodic Behavior of Zn-Al-Be Alloys in NaCl Solution and the Influence of Be on Structure Reza Amini , Ziadolla Obidov , Izatulla Ganiev , Mohammad Razazi 1 2 2 1 1 Department of Material Science and Engineering, Islamic Azad University, Majlesi Branch, Isfahan, Iran; 2 Tajikistan Academy of Sciences, Chemistry Institute, Dushanbe, Tajikistan. Email: reza.amini@mail.ru Received October 24 , 2011; revised February 28 , 2012; accepted March 9 , 2012 th th th ABSTRACT Potentiodynamic results of anodic behavior of Zn5Al and Zn55Al alloys, alloyed with Beryllium in the ambience of NaCl electrolyte and their microstructures are studied. They showed that a small addition of Beryllium (0.005 - 0.05 wt%) improves the corrosion resistance of Zn5Al and Zn55Al original alloys to 2 - 3 times by changing grains shape to spherical and changing sizes to small grains. The proposed composition of Zinc-Aluminum alloy, which contains of Beryllium, can be used as anodic coatings to protect steel products and constructions against corrosion. Keywords: Zn5Al; Zn55Al; Beryllium; NaCl Solution; Corrosion Resistant 1. Introduction 2. Experimental Procedure Metal coatings applied to surface of products by different methods. Currently, the method is used to protect steel and cast iron against the corrosion. Choice of coatings and application of techniques are determined by the op- erating requirements of reliability and durability of struc- tures [1]. For many years, Zinc coating has been widely used to