学兔兔 画 铸造工程 Foundry Engi neeri ng 电动机托架湿型砂铸造工艺 陈雪松 (大江信达车辆股份有限责任公司铸造公司，重庆 401 321) 摘要：为采用湿型砂气冲造型工艺生产电动机托架铸件，基于铸件结构和生产条件，分析了分 型面、浇注位置、浇注系统等工艺要素，确定了托架铸件的工艺方案；针对浇注后出现的铸件 表面缩陷和夹砂缺陷，从熔炼、型砂、浇冒口设置等方面进行了改进和调整。改进后的工艺经 生产验证，铸件表面缩陷和膨胀夹砂现象得以彻底消除，效果明显，系列铸件的工艺出品率可 达8 5％以上。 关键词：平面铸件；湿型砂；铸造工艺 中图分类号：TG250．6 文献标识码：B 文章编号：1 673-3320(2013)05-0030-03 Casting Process of Bracket for Electromotor with Green Molding Sand Chen Xuesong (Foundry Branch of Dajiang Xinda Vehicle Co．，Ltd．，Chongqing 401 321，China) Abstract：In order to produce the bracket castings for electromotor with green sand air~mpact molding process，the process factors，including mold joint，pouring position and gating system，were analyzed upon casting structure and production condition．The process scheme of bracket was determined． To the depression and scab on casting surface after pouring，the process was improved and adjusted from smelting，molding sand and ingate and riser setting．The improved process through production verification shows that the depression and scab on casting surface is completely removed，which effects are obvious．The rate of qualified castings is increased up to 85％． Key words：planar casting；green molding sand；casting process 公司为某日资电动机器有限公司开发高速 达77 mm，存在一定的壁厚悬殊。考虑个别非加 电梯薄型电动机托架。该类托架有多个型号，属 工铸件尺寸650 mm、158一 mm、(143±1)mm 于系列铸铁产品。系列铸件的最大轮廓尺寸为 的公差要求达到CT8级，只有采用金属模、湿型 730 mm×650 mm×(141～265)mm，铸件质量 砂气冲造型线的生产方式，才有可能满足铸件的 157～185 kg不等，材质的化学成分、显微组织、 尺寸精度要求。 力