低碳钢变形奥氏体动态再结晶行为及组织演变.pdfVIP

下半月出版 Material Heat Treatmentl材料热处理技术 低碳钢变形奥氏体动态再结晶行为及组织演变 张勇明，自月番 (江西交通职业技术学院机电工程系，江西南昌 330013) 摘 要:在单道次压缩变形实验中，采用 Gleeble-1500 热模拟实验机测定了低碳钢SS400 和 T510L 钢在 950-1050.C 、 0.5/s 、 5/s 、变形量 80%条件下的热变形行为，研究了变形温度、变形速率对实验钢再结晶行为及再结晶后奥氏体晶粒尺 寸的影响，建立了低碳钢的动态再结晶模型。 关键词:动态再结晶;低碳钢;奥氏体晶粒尺寸:变形条件 中图分类号:TG142.31 文献标识码:A 文章编号: 1001-3814(2012)04-0045-04 Austenite Dynamic Recrystallization and Microstructure Evolution of Low Carbon Steel ZHANG Yongming, BAI Yuexiang (Department of Elec创cal and Mechanical Engine喝ring， Jiangxi Vocation and Technical College of Communication , Nanchang 330013 , China) Abstract:Dynamic recrystallization behaviors of low carbon steel were studied using Gleeble-1500 thermornechanical sirnulator at 950 C -1050 .C , strain rate of O.5/s and 5/s, strain up to 0.8. The influences of deformation ternperature and rate on recrystallization behavior and austenite grain size of experiment steel were studied and the d归amic mathematical rnodel of recrystallization behavior was establish\!d. Key words :dynarnic recrystallization; low carbon steel; austenite gr百in size; deformation condition 奥氏体变形、再结晶是奥氏体组织演变过程，在 酸过饱和溶液浸蚀，用光学显微镜观察不同变形条 件下的变形奥氏体组织。 此过程中，奥氏体的状态发生变化，这些变化必然对 变形后奥氏体的相变行为及相变组织、性能产生很 2 实验结果 大的影响[1]。为了研究低碳钢 SS400 和 T510L 的动 2.1 实验钢的应力-应变曲线 态再结晶情况，在 Gleeble-1500 热模拟机上进行动 图 1~3 为低碳钢不同应变速率、不同温度下变 态再结晶模拟试验，从而研究再结晶规律并为实际 形过程的应力-应变曲线。可看出，钢的应力-应变 生产提供理论依据。 曲线由几个阶段组成:①当塑性变形量较小时，随变 1 实验方法