并发沉淀析出对Al-Mn变形铝合金再结晶织构的影响.pdfVIP

Joumal of Southeast University (English Edition) Vo l. 31 , No. 4 , pp. 501 - 505 Dec.2015 ISSN 1003一7985 Effect of concurrent precipitation on recrystallization textures in commercial Al-Mn alloys l l l l l 2 Tu Yiyou Huang Linghui Sun Zhongyue Zhou Xuefeng Jiang Jianqing . ( 1 School of Materials Science and Engineeri吨， Southeast University , N叫ing 211189 , China) (2Nanjing University of Information Science and Technology, Nanjing 21∞44， China) Ab西tract: The effect of concurrent precipitation on has been proved to aid explanations of 由e recrystallization r巳crystallization textures in AA 3∞3 a1urninum a1loys was textures of aluminum alloys; this strategy is based on investigated using X-ray diffraction and electron backscattering growth selection from a limited spectrum of preferentially diffraction( EBSD) ana1yses. A weak recrysta1lization texture formed nucleus orientations[2， 6叮J was observed in the AA 3∞3 a1loy annea1ed at 783 K due t。 The recrystallization texωre of most aluminum alloys is 由e high annea1ing temperature. Under the same conditions , characterized by a cubic orientation with scattering along extremely high P {O 11 }111) recrystallization text町es were the rolling direction toward the Goss orientation. As-de- detected in the AA 3∞3 a1loy added with O. 39% Sc. Based on