不锈钢管接头的失效分析及其质量改进.pdfVIP

~失效分析~ 不锈钢管接头的失效分析及其质量改进 陆频，程永红 （宝钢工业检测公司，上海 201900） 摘　要：通过实例对1Cr18Ni9Ti钢管接头的泄漏事故进行了分析，结果发现，管接头的早期失效是由于其固 溶处理不良所致。介绍了从表面产生沿晶腐蚀，晶粒相互脱离，大量沿晶裂纹形成，其中一些裂纹扩 展，直至该管接头开裂失效的全过程。 关键词：失效分析；不锈钢；管接头；固溶处理 中图分类号：TG142.71　　文献标识码：B　　文章编号：1008-1690(2006)02-0056-004 Failure Analysis on Union of Stainless Steel and Improvement on Its Quality LU Pin, CHENG Yong-hong (Baosteel Industrial Detection Co., Shanghai 201900) Abstract: The leakage accident of pipe union of 1Cr 18Ni9Ti steel was analyzed through a living example. It was revealed that the early failure of pipe union arose from poor solution treatment. The whole process of failure of the pipe union from occurrence of intergranular corrosion on the surface, divorcement of one grain from another , formation of a large amount of intergranular cracks,extension of some of the cracks untill complete failure of the pipe union was introduced. Key Words: failure analysis; stainless steel; union; solution treatment 1　引言 之一时)就漏水的产品。 钢铁厂连续铸造车间在生产连铸板坯时，对高 2　理化检验 温坯料的表面要及时均匀地喷水冷却，使其表面迅 2.1　化学成分分析 速凝壳，并使壳层厚度均匀和达到一定尺寸。由于 首先对两个样品的化学成分进行化验，结果表 板坯规格不同，喷水部位要经常调整、移动，因 明，实物化学成分均在1Cr18Ni9Ti钢成分范围之 此，冷却水管采用金属软管制作，接头采用不锈钢 内，属奥氏体不锈钢，检测结果见表1。 材料。软管和接头处于高温、雾汽和粉尘的环境之 2.2　宏观检查 中，服役条件恶劣。通常，软管和接头使用到一定 软管接头样品的形貌见图1-1所示。在对样品的 周期時，必须更换。因为，如果使用中途漏水，提 目视检查时发现2号样品存在数条已经贯穿的纵向裂 前失效，则造成板坯表面的冷却速度不均匀，严重 缝及漏水的痕迹，裂纹打开后的断口形貌见图1-2所 时，使连铸板坯发生横裂、纵裂等质量事故，因 示，断口较为粗造，晶粒较粗，有沿晶断裂的特 此，厂方对此历来均十分重视。 征。 2005年1月初，接到某厂连铸车间的软管不锈 2.3　金相观察 钢接头2件。厂方反应，其中一号接头样品为正常使 来样经线切割，每只试样取横向和纵向截面分 用至更换周期时下机的产品；2号接头样品为提前失 别镶嵌，然后试样经磨削，抛光，采用三氯化铁盐 效，仅使用15天左右(约使用至正常更换周期的三分 酸酒精溶液进行腐蚀，在腐蚀过程中发现，同样是 表1管接头的化学成分(wt%) Tablr 1 Chemical composition of the union (wt%) 化学元素 C Si Mn Cr